Cactus Industrial Epoxy Surface And Wet Tolerant Protective Coating
- Chemical Family
- Epoxy & Epoxy Derivatives
Cactus Industrial Epoxy Surface And Wet Tolerant Protective Coating is a high-performance solvent-free, two-pack epoxy mastic designed to provide corrosion resistance and abrasion protection in extreme service applications. This specially designed epoxy system is capable of application and curing underwater and form a tough protective barrier. It provides outstanding adhesion on wet blasted surfaces.
Product families
- Protective Coatings
Other characteristics
- Features
Abrasion Resistant, Chemical Resistant, Corrosion Resistant, Good Barrier Properties, High Performance, Low Temperature Strength, Non Wetting, Skid Resistant
- Product Type
2K (2 component) Coating, Epoxy Coating, Solventless & High Solids Coating; 2K (2 component) Coating; Epoxy Coating; Solventless & High Solids Coating
- Application Area
- Bridges, Pipes
- Bridges
- Pipes
- Application Method
- Brush, Roller, Spray
- Compatible Substrates & Surfaces
- Concrete, Metal, Steel
- Finish
Gloss / Matte; Surface finish will be matte when coating is underwater or surface covered by water during curing.
- Mixing
Mix Part A thoroughly then add in Part B and continue to mix till homogeneous.; Do not mix more materials than the quantity to be consumed within the pot life.
- Markets
- Automotive & Transportation
- Building & Construction
- Paints & Coatings
- Cleaning
Clean all application tools with relevant cleaner immediately after use.
- Pot Life
- 45 minutes at 30°C.
- Varies with temperature.
- Thinning
Thinning is not allowed for underwater applications.. For applications above water to overcome issue related to workability of spray equipment, not more than 10% by weight of relevant Thinner is allowed.
- PACKAGING
- Part A - 4 kg
- Part B - 1 kg
- Shelf LIfe
- Part A - 2 years
- Part B - 1 year
- Performance
Durable - Tough and impermeable layer with excellent resistance against salt and water.; Zero Solvent-freet free product.; Suitable for cold sweating steel surfaces.; Chemical resistant - Good resistanca e against wide range of chemicals.; Under -water curing - capable of applicationunderwater under water.; Adhesion - Excellent adhesion to dry and wet surfaces.; Cures at low temperature.
- Technology
- Ready-to-Use Products
- Labeling Claims
- Environmentally Friendly
- Recommended Use
Designed to provide corrosion protection for metal and concrete structures in offshore marine and petrochemical services, sheet piles, underground and submarine pipes, waste water tanks, jetty piles, underground tanks and other structural steel that requires protection against corrosion in aggressive environment.. It is most suitable for rehabilitation of corroded steel and concrete structures in tidal zone and below water line where conventional protective coatings are not applicable. It is an ideal maintenance coating for cold pipes with condensation.
- Application Methods
- Brush
- Roller
- Spray
Technical data
Table 1 of 3
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Solids by Volume | 100.0 | % |
| Thickness (DFT Per Coat) | 150.0 | microns |
| Drying Time Touch Dry | 4.0 | hours |
| Drying Time Topcoat | 12.0 | hours |
| Drying Time Full Cure | 7.0 | days |
Table 2 of 3
1 row| Characteristic | Value |
|---|---|
| Mixing Ratio by Weight | 4.0 |
Table 3 of 3
1 row| Characteristic | Value |
|---|---|
| Mixing Ratio by Weight | 1.0 |