Cactus Industrial Urethane 80 Rubber Repair And Protection
- Chemical Family
- Polyurethanes (PU)
Cactus Industrial Urethane 80 Rubber Repair And Protection are 2-component polyurethanes that cure at room temperature to tough rubber-like materials, remaining flexible at temperatures down to even -60°C. WEICON Urethanes adhere to a variety of materials such as metals, concrete, rubber, wood, fiberglass and many others. They are also suitable as flexible coatings in connection with WEICON Plastic Metal epoxy systems. Due to their low sensitivity to humidity they can also be used for coatings in thin layers and have a remarkably high tensile and tear strength.
Product families
Applications
- Concrete Coatings & Stains
- Wood Coatings & Finishes
Product Families
- Protective Coatings
Other characteristics
- Features
Excellent Toughness, Good Tear Strength, High Tensile Strength, Low Temperature Flexibility
- Product Type
- 2K (2 component) Coating, Repair Paint
- 2K (2 component) Coating
- Repair Paint
- Application Area
- Tanks, Vacuum Pumps
- Tanks
- Vacuum Pumps
- Compatible Substrates & Surfaces
Concrete, Elastomers & Rubbers, Fiberglass, Metal, Wood
- Markets
- Paints & Coatings
- Pot Life
- At 20°C +68°F for 10ml material.
- 25 minutes.
- Conditions
Final Strength* - or after 24 hours at room temperature + 4 hours 70°C.
- Cure
- Air Dry
- Technology
- Ready-to-Use Products
- Available Sizes
- 10518005
- Urethane 80 0.5 kg
- Temperature Resistance
- -60 to +90 °C
- ISSA-Code 75.509.42
- IMPA-Code 81.29.63
- Ready to Use Product Features
- Excellent Toughness
- Good Tear Strength
- High Tensile Strength
- Low Temperature Flexibility
- Compatible Substrates and Surfaces
- Concrete
- Elastomers & Rubbers
- Fiberglass
- Metal
- Wood
Technical data
Table 1 of 3
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mixture by Weight (Resin) | 100.0 | — |
| Viscosity (25°C, Resin) | 5000.0 | mPa·s |
Table 2 of 3
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mixture by Weight (Hardener) | 80.0 | — |
| Viscosity (25°C, Hardener) | 190.0 | mPa·s |
Table 3 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness | 80.0 | Shore A | — |
| Base | Polyurethane | — | — |
| Density Mixture | 1.0 | g/cm | — |
| Viscosity (Mixture, 25°C) | 2000.0 | mPa·s | — |
| High Mechanical Load Capacity (Detachable After) | 12 - 20 | hours | — |
| Final Strength* (100%, After) | 48.0 | hours | — |
| Tensile Strength | 8.0 | MPa | ISO 37 |
| Elongation at Break | 600.0 | % | ISO 37 |
| Resistance to Further Tearing | 15.0 | — | — |