RECKLI Epoxy WST
- Chemical Family
- Epoxy & Epoxy Derivatives
RECKLI Epoxy WST is a liquid, transparent, solvent-free two-component epoxy resin with high compressive strength and dimensional stability under heat. It is wellcuring, even in thin layers.
Properties
- Physical Form
- Liquid
Product families
Applications
- Exterior & Body
- Interior
- Wallcoverings & Decorative Laminates
Product Families
- Epoxies
Other characteristics
- End Uses
- Thin Coatings
- Polymer Name
- Epoxy Resins & Compounds
- Safety
Protect skin and eyes from material splashes. Provide sufficient ventilation in the working place. Please consult the relevant safety data sheet and attend to the indications on the label of the package regarding the Dangerous Goods Regulation. This pamphlet is intended solely as an application directive. It does not claim to be binding and valid for all modes of application. A preliminary test under operation conditions is highly recommended.. This pamphlet replaces all previously published pamphlets concerning RECKLI Epoxy WST, stating them as no longer being valid.
- Markets
- Automotive & Transportation
- Building & Construction
- Storage
Store in a dry place at room temperature. RECKLI Epoxy WST is storable for _x0011_6 months from delivery when kept in the closed original packaging at about _x001f_18°C. Opened drums must be closed airtight right after use.
- Appearance
- Transparent
- Processing
Add the hardener (B) to the base component (A) and mix them homogenously. Transfer the mixture into a second receptacle and stir it up again. Thereby the incorporation of larger amounts of air should be avoided. Fillers should be preferably added to the mixture rather than to the base component before mixing. Once mixed, the processing of the material must be completed within the pot life (15 _x0013_– _x001e_20 minutes). Mixing larger quantities decreases the processing time.
- Cure
- Heat Cure
- Technology
- Plastics
- Labeling Claims
- Solvent-free
- Packaging Size
- Double drum: 4_x001d_ kg | Double can: 0.8 kg
- The hardener is enclosed in the lid.
- Material Features
- Chemical Resistant
- Dimensional Stability
- Good Compressive Strength
- Low Temperature Curing
- Chemical Resistance
- Calcium Chloride
- Citric Acid
- Edible Oils
- Isopropyl Alcohol
- Tartaric acid
- Water
- White Spirit
- Xylene
- Surface Preparation
For coatings or adhesions, the substrate must be stable, sound, dry, clean and free of oil, grease or wax.
- Plastics and Elastomers End Uses
- Thin Coatings
- Plastics and Elastomers Functions
- Filler
Technical data
Table 1 of 1
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mixing ratio (base : hardener) | 7:1 | — | (according to weight) |
| Workable temperature | -20 | °C | — |
| Viscosity of base component | 2500 | mPa.s | ISO 2555 |
| Viscosity of base component | 2500 | mPa.s | !SO 2555 |
| Pot life (200-g mixture at +21°C) | 15-20 | minutes | — |
| Earliest demoulding (at +21°C): | 24 | hours | — |
| Full chemical and mechanical loading after: | 7 - 10 | days | — |
| Density | 1.3 | g/cm³ | — |
| Hardness | 45 | Shore A | DIN 53505 |
| Ball impression hardness | 55 - 60 | N/mm² | DIN 53456 |
| Dimensional stability under heat | 60 | °C | DIN 53462 |
| Heat Resistance (Dry Heat) | approx. 100 | °C | — |