RECKLI Flooring Resin EP
- Chemical Family
- Epoxy & Epoxy Derivatives
RECKLI Flooring Resin EP is a transparent, solvent-free, low-viscous twocomponent epoxy resin. On exposure to direct sunlight or UV irradiation, the resin is gradually yellowing; however, without degradation of mechanical properties.
Properties
- Physical Form
- Liquid
Product families
Applications
- Construction Adhesives
Product Families
- Epoxies
Other characteristics
- End Uses
- Thin Coatings
- Polymer Name
- Epoxy Resins & Compounds
- Safety
Protect skin and eyes from material splashes. Provide sufficient ventilation in the working place. Please consult the relevant safety data sheet and attend to the indications on the label of the package regarding the Dangerous Goods Regulation. This pamphlet is intended solely as an application directive. It does not claim to be binding and valid for all modes of application. A preliminary test under operation conditions is highly recommended.. This pamphlet replaces all previously published pamphlets concerning RECKLI Flooring Resin EP, stating them as no longer being valid.
- Markets
- Building & Construction
- Storage
Store in a dry place at room temperature. RECKLI Flooring Resin EP is storable for 6 months from delivery when kept in the closed original packaging at about _x001e_18°C. Opened drums must be closed airtight right after use.
- Appearance
- Transparent
- Processing
Add the hardener (B) to the base component (A) and mix them homogenously. Transfer the mixture into a second receptacle and stir it up again. Thereby the incorporation of larger amounts of air should be avoided. Fillers should be preferably added to the mixture rather than to the base component before mixing. Once mixed, the processing of the material must be completed within the pot life (_x0013_40 - 50 minutes). Mixing larger quantities decreases the processing time.
- Cure
- Heat Cure
- Technology
- Plastics
- Packaging Type
- Cans
- Labeling Claims
- Solvent-free
- Packaging Size
- Pair of canisters
- _x001e_8 kg;
- Double can
- 0.8 kg (the hardener is enclosed in the lid).
- Material Features
- Chemical Resistant
- Dimensional Stability
- Good Compressive Strength
- Low Temperature Curing
- Low Viscosity
- Chemical Resistance
- Calcium Chloride
- Citric Acid
- Edible Oils
- Isopropyl Alcohol
- Tartaric acid
- Water
- White Spirit
- Xylene
- Surface Preparation
For coatings or adhesions, the substrate must be stable, sound, dry, clean and free of oil, grease or wax.
- Plastics and Elastomers End Uses
- Thin Coatings
- Plastics and Elastomers Functions
- Binder
- Resin
Technical data
Table 1 of 1
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mixing ratio (base : hardener) | 3:1 | — | (according to weight) |
| Workable temperature | -20 | °C | — |
| Viscosity of the mixture | approx. 350 | mPa.s | !SO 2555 |
| Pot life (200-g mixture at +21°C) | approx. 40 - 50 | minutes | — |
| Full chemical and mechanical loading after: | 10 - 12 | days | — |
| Density | 1.1 | g/cm³ | — |
| Hardness | approx. 73 | Shore A | DIN 53505 |
| Ball impression hardness | 50 - 55 | N/mm² | DIN 53456 |
| Dimensional stability under heat | 40 | °C | DIN 53462 |
| Heat Resistance (Dry Heat) | 100 | °C | — |