RECKLI Epoxy GF Filler
- Chemical Family
- Epoxy & Epoxy Derivatives
RECKLI Epoxy GF Filler is a pasty, glass fiber reinforced, solvent-free twocomponent epoxy resin with high impact resistance as well as compressive- and flexural strength. It is almost shrinkage-free and insensitive to moisture, thus being applicable on slightly humid surfaces. The addition of further filling material is not recommended.
Product families
- Epoxies
Other characteristics
- Polymer Name
- Epoxy Resins & Compounds
- Safety
Protect skin and eyes from material splashes. Provide sufficient ventilation in the working place. Please consult the relevant safety data sheet and attend to the indications on the label of the package regarding the Dangerous Goods Regulation. This pamphlet is intended solely as an application directive. It does not claim to be binding and valid for all modes of application. A preliminary test under operation conditions is highly recommended.. This pamphlet replaces all previously published pamphlets concerning RECKLI Epoxy GF Filler, stating them as no longer being valid.
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Paints & Coatings
- Storage
Store in a dry place at room temperature. RECKLI Epoxy GF Filler is storable for 6 months from delivery when kept in the closed original packaging at about _x001f_18°C. Opened drums must be closed airtight right after use.
- Processing
Before processing, the base component has to be stirred up thoroughly. Add the hardener (B) to the base component (A) and mix them homogenously. Transfer the mixture into a second receptacle and stir it up again. Once mixed, the processing of the material must be completed within the pot life (15 – _x001e_20 minutes). Mixing larger quantities decreases the processing time.; For making supporting molds, RECKLI Epoxy GF Filler is applied with a trowel or a scraper up to 5 mm thickness. To increase the stiffness and the tear strength, additional glass fabric can be embedded in the application. To protect against injuries, protruding glass fibers and sharp edges must be removed. When fresh, the material can be smoothed by hand with the help of soap solution. To avoid skin contact, wear disposable gloves. When cured, the surface can be smoothed with a grinding machine. Avoid breathing grinding dust; if necessary, wear a dust mask.; Supports or reinforcements out of steel or timber can be glued to the plastic cap with RECKLI GF Filler as well. To achieve good adhesion, bare metal or coated wood must be roughened by grinding.; Depending on the mold's size and nature, the complete formwork can earliest be disassembled after 7 – 8_x001f_ hours. Earliest mechanical loading is possible after 12_x001e_ – 24_x001e__x001d_ hours.
- Consumption
- 1.25 kg/m² per mm thickness
- Cure
- Chemical Cure
- Technology
- Plastics
- Labeling Claims
- Solvent-free
- Packaging Size
double drum: _x001d_4.5 kg | double can: 0.9 kg The hardener is enclosed in the lid.
- Fillers Included
- Glass Fiber
- Material Features
- Good Impact Strength
- Good Shrinkage Resistance
- High Flexural Modulus
Technical data
Table 1 of 1
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mixing ratio (base : hardener) | 8:1 | — | (according to weight) |
| Workable temperature | -20 | °C | — |
| Pot life (200-g mixture at +21°C) | approx. 15 - 20 | minutes | — |
| Earliest demoulding (at +21°C): | 7 - 8 | hours | — |
| Earliest mechanical loading after | 12 - 24 | hours | — |
| Density | 1.25 | g/cm³ | — |
| Dimensional stability under heat | 60 | °C | — |
| Heat Resistance (Dry Heat) | 100 | °C | — |
| Heat Resistance (Under Concrete) | 80 | °C | — |