RECKLI Epoxy Flex Filler
- Chemical Family
- Epoxy & Epoxy Derivatives
RECKLI Epoxy Flex Filler is a pasty, solvent-free, fast curing two-component epoxy resin, almost shrinkage-free. It is compatible with common epoxy resin coatings.
Product families
Applications
- Industrial — Maintenance
- Repair & Overhaul
- Body Shop & Repair
- Floor Coatings
- Fillers Levellers & Joints
- Floor Coatings
Product Families
- Epoxies
Other characteristics
- Polymer Name
- Epoxy Resins & Compounds
- Safety
Protect skin and eyes from material splashes. Avoid breathing vapor that may accumulate in the can after prolonged storage. Please consult the relevant safety data sheet and attend to the indications on the label of the package regarding the Dangerous Goods Regulation. This pamphlet is intended solely as an application directive. It does not claim to be binding and valid for all modes of application. A preliminary test under operation conditions is highly recommended.. This pamphlet replaces all previously published pamphlets concerning RECKLI Epoxy Flex-Filler, stating them as no longer being valid.
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Paints & Coatings
- Storage
Store in a dry place at room temperature. RECKLI Epoxy Flex-Filler is storable for 6_x0012_ months from delivery when kept in the closed original packaging at about _x000f_18°C. Opened drums must be closed airtight right after use.
- Processing
Before processing, both components have to be stirred up thoroughly. The hardener occasionally forms salts in contact with the air. These cannot be incorporated and must be removed before further proceeding. Add the hardener B) to the base component (A) and mix them homogenously until a uniformly gray color is reached. The material on the walls of the mixing cup must be included in the mixing process as well. According to the application thickness, RECKLI Epoxy Flex-Filler is grindable after _x000f_½ – _x0010_2 hours, loadable after 3 – 4_x001e_ hours.
- Cure
- Chemical Cure
- Technology
- Plastics
- Labeling Claims
- Solvent-free
- Packaging Size
- Pair of cans: _x000f_1 kg.
- Material Features
- Fast Curing
- Surface Preparation
The substrate must be stable, sound, dry, clean and free from oil, grease or wax. Plastics, such as phenolic or epoxy resins, must be roughened by grinding. The adhesion to other plastics should be established in a preliminary test.. Joints between panels should be 3– 5 mm wide. In the area of the joint, the panels have to be firmly attached to the underground or, if necessary, screwed before filling the gap.
- Plastics and Elastomers Functions
- Filler
Technical data
Table 1 of 1
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mixing ratio (base : hardener) | 1:1 | — | (according to weight) |
| Workable temperature | -20 | °C | — |
| Pot life (200-g mixture at +21°C) | approx. 4 - 5 | minutes | — |
| Grindable after | 1.5 - 2 | hours | — |
| Earliest loading (at +21°C) | 3 - 4 | hours | — |
| Density | 1.85 | g/cm³ | — |