Teldene® H25FBA
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Teldene® H25FBA is used as extrusion of fibers bulk continuous filaments (BCF) and continuous filaments (CF) such as carpet and upholstery. Also, staple fiber and non-woven.
Properties
- Physical Form
- Granules
- Solid
Product families
- Polyolefins
Other characteristics
- Brand
- Teldene
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 25.0 - 25.0 g/10 min
- Processing Methods
Coextrusion, Extrusion, Fibers Extrusion, Filament Extrusion
- Markets
- Automotive & Transportation
- HI&I Care
- Industrial
- Technology
- Plastics
- Food Regulations
This product is defined as a preparation under specific food contact regulation. Detailed information will be provided in a relevant document "Regulatory Compliances Product Declaration" upon request.
- Material Features
- Broad Processing Window
- Good Mechanical Properties
- Key Characteristics
Formulated with anti-gas fading stabilization package; Reactor grade (no peroxide added)
- Storage and Handling
Polypropylene resin should be stored to prevent a direct exposure to sunlight and heat. The Product. estimated shelf life is one year starting from production date, adequate humidity below 80%, and temperature below 40°C. Customers might not fully follow the optirnal storage condition, hence the shelf life recommended at customer site is six months only as received.
- Processing Conditions
Average extruder temperature range may be kept between 240- 260°C.
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Coextrusion
- Extrusion
- Fibers Extrusion
- Filament Extrusion
Technical data
Table 1 of 1
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density 23°C | 0.9 | g/cm³ | ISO. 1183 |
| Melt Flow Rate (MFR) 230°C/2.16 kg | 25 | g/10-min | ASTM D 1238-13 |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Tensile Stress at Break 50-mm/min | 36 | MPa | ISO 527 |
| Tensile Strain at Break 50-mm/min | min. 50 | % | ISO 527 |
| Tensile Strain at Yield 50-mm/min | 10 | % | ISO 527 |
| Heat Deflection Temperature 0.45 MPa Un-annealed | 89 | °C | ISO 75B |
| Vicat Softening Temperature A50 (50°C/h 10N) | 155 | °C | ISO 306 |
| Izod Notched 23°C | 2.2 | KJ/㎡ | — |