Teldene® H12ML
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Teldene® H12ML is used as injection molding for production of furniture, crates, containers, caps and closures and general purpose is used as injection molding articles.
Properties
- Physical Form
- Granules
- Solid
Product families
- Polyolefins
Other characteristics
- Brand
- Teldene
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 12.0 - 12.0 g/10 min
- Processing Methods
- Injection Molding
- Markets
- Consumer Goods
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Special Features
Shows broad processing window while providing good mechanical properties
- Material Features
- Broad Processing Window
- Food Contact Acceptable
- Good Flow
- Good Mechanical Properties
- High Stiffness
- Key Characteristics
Good flow properties, High Stiffness; Food contact approval for specific applications (refer to NATPET)
- Storage and Handling
Polypropylene resin should be stored to prevent a direct exposure to sunlight and heat. The Product estimated shelf life is one year starting from production date, adequate humidity below 80%, and temperature below 40°C. Customers might not fully follow the optimal storage condition, hence the shelf life recommended at customer site is six months only as received.
- Processing Conditions
Average extruder temperature range may be kept between 240 - 260°C.
- Plastics and Elastomers End Uses
- Caps
- Closures
- Containers
- Crates
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density 23°C | 0.9 | g/cm³ | ISO 1183 |
| Melt Flow Rate (MFR) 230°C/2.16 kg | 12 | g/10-min | ASTM D 1238-13 |
| Flexural Modulus | 1500 | MPa | ISO 178 |
| Tensile Stress at Break 50-mm/min | 26 | MPa | ISO 527 |
| Tensile Stress at Yield 50-mm/min | 35 | MPa | ISO 527 |
| Tensile Strain at Break 50-mm/min | min. 50 | % | ISO 527 |
| Tensile Strain at Yield 50-mm/min | 13 | % | ISO 527 |
| 1200 netched 23°C | 3.9 | KJ/㎡ | ISO 180 |
| Heat Deflection Temperature 0.45 MPa Un-annealed | 91 | °c | ISO 75B |
| Vicat Softening Temperature A50 (50°C/h 10N) | 152 | °c | ISO 306 |
| Tensile Modulus 1-mm/min | 1550 | MPa | ISO 527 |