- Chemical Family
- PolyolefinsPolypropylenes (PP)
Teldene® H03ML is used as injection molding for house wares, toys, small appliance parts, Raffia and automotive compounding.
Properties
- Physical Form
- Granules
- Solid
Product families
- Polyolefins
Other characteristics
- Brand
- Teldene
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 3.2 - 3.2 g/10 min
- Processing Methods
- Coextrusion, Extrusion, Injection Molding
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Food Regulations
This product is defined as a preparation under specific food contact regulation. Detailed information will be provided in a relevant document "Regulatory Compliances Product Declaration" upon request.
- Material Features
- Broad Molecular Weight Distribution
- Broad Processing Window
- Food Contact Acceptable
- Good Mechanical Properties
- Good Processability
- Good Stiffness
- Key Characteristics
Good processability, Good Stiffness; Bi-Modal grade, broad MWD; Food contact approval for specific applications (refer to NATPET)
- Storage and Handling
Polypropylene resin should be stored to prevent a direct exposure to sunlight and heat. The Product estimated shelf life is one year starting from production date, adequate humidity below 80%, and temperature below 400 C. Customers might not fully follow the optimal storage condition, hence the shelf life recommended at customer site is six months only as received.
- Processing Conditions
Average extruder temperature range may be kept between 240-260 °C .
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Coextrusion
- Extrusion
- Injection Molding
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density 23°C | 0.9 | g/cm³ | ISO 1183 |
| Melt Flow Rate (MFR) 230°C/2.16 kg | 3.2 | g/10-min | ASTM D 1238-13 |
| Flexural Modulus | 1470 | MPa | ISO 178 |
| Tensile Stress at Break 50-mm/min | 23 | MPa | ISO 527 |
| Tensile Stress at Yield 50-mm/min | 34 | MPa | ISO 527 |
| Tensile Strain at Break 50-mm/min | min. 50 | % | ISO 527 |
| Tensile Strain at Yield 50-mm/min | 12 | % | ISO 527 |
| IZ0d Notched 23°C | 5.1 | KJ/㎡ | ISO 180 |
| Heat Deflection Temperature 0.45 MPa Un-annealed | 85 | °¢ | ISO 75B |
| Vicat Softening Temperature A50 (50°C/h 10N) | 154 | °c | ISO 306 |
| Tensile Modulus 1-mm/min | 1500 | MPa | ISO 527 |