Teldene® H03TF
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Teldene® H03TF In-line and off-line thermoforming for fruit baskets, trays, transparent drinking cups and containers.
Properties
- Physical Form
- Granules
- Solid
Product families
- Polyolefins
Other characteristics
- Brand
- Teldene
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 3.7 - 3.7 g/10 min
- Additives Included
- Anti-Static Agent, Nucleating Agent
- Anti-Static Agent
- Nucleating Agent
- Processing Methods
- Thermoforming
- Markets
- Consumer Goods
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Food Regulations
This product is defined as a preparation under specific food contact regulation. Detailed information will be provided in a relevant document "Regulatory Compliances Product Declaration" upon request
- Material Features
- Broad Processing Window
- Dimensional Stability
- Excellent Transparency Properties
- Food Contact Acceptable
- Good Mechanical Properties
- Good Organoleptic Properties
- Good Processability
- Isotropic Shrinkage Behavior
- Key Characteristics
Nucleated homopolymer, contains anti-static agent; Excellent transparency and processability; Excellent stiffness and dimensional stability; Excellent isotropic shrinkage control; Excellent for deep thermoforming application; Good organoleptic properties; Food contact approval for specific applications (refer to NATPET)
- Storage and Handling
Polypropylene resin should be stored to prevent a direct exposure to sunlight and heat. The Product es-timated shelf life is one year starting from production date, adequate humidity below 80%, and tempera-ture below 400 C. Customers might not fully follow the optimal storage condition, hence the shelf life recommended at customer site is six months only as received.
- Processing Conditions
Average extruder temperature range may be kept between 230- 2400 °C
- Plastics and Elastomers End Uses
- Containers
- Cups
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Thermoforming
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density 23°C | 0.9 | g/cm³ | ISO 1183 |
| Melt Flow Rate (MFR) 230°C/2.16 kg | 3.7 | g/10-min | ASTM D 1238-13 |
| Flexural Modulus | 1720 | MPa | ISO. 178 |
| Tensile Stress at Break 50-mm/min | 27 | MPa | ISO 527 |
| Tensile Stress at Yield 50-mm/min | 37 | MPa | ISO 527 |
| Tensile Strain at Break 50-mm/min | min. 50 | % | ISO 527 |
| Tensile Strain at Yield 50-mm/min | 9 | % | ISO 527 |
| 120d notched 23°C | 5.1 | KJ/㎡ | Iso 180 |
| Heat Deflection Temperature 0.45 MPa Un-annealed | 90 | °C | ISO 75B |
| Vicat Softening Temperature A50 (50°C/h 10N) | 155 | °C | ISO 306 |
| Tensile Modulus 1-mm/min | 1600 | MPa | ISO 527 |