Teldene® H03BPMP
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Teldene® H03BPMP is used as is used as extrusion BOPP films at very high speed with excellent processability, thermoforming, raffia and automotive compounding.
Properties
- Physical Form
- Film
- Granules
Product families
- Polyolefins
Other characteristics
- Brand
- Teldene
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 3.0 - 3.0 g/10 min
- Processing Methods
- Coextrusion, Extrusion, Thermoforming
- Markets
- Automotive & Transportation
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Food Regulations
This product is defined as a preparation under specific food contact regulation. Detailed information will be provided in a relevant document "Regulatory Compliances Product Declaration" upon request.
- Material Features
- Broad Processing Window
- Excellent Transparency Properties
- Food Contact Acceptable
- Good Mechanical Properties
- Good Optical Properties
- Good Processability
- High Film Stiffness
- High Gloss
- Key Characteristics
Easy processing, good optical characteristics; Does not contain any slip or anti-blocking agents; Calcium stearate free; Very good film profile; High speed film production; High transparency and gloss with high stiffness and strength; Food contact approval for specific applications (refer to NATPET)
- Storage and Handling
Polypropylene resin should be stored to prevent a direct exposure to sunlight and heat. The Product estimated shelf life is one year starting from production date, adequate humidity below 80%, and temperature below 400 C. Customers might not fully follow the optimal storage condition, hence the shelf life recommended at customer site is six months only as received.
- Processing Conditions
Average extruder temperature range may be kept between 240- 2600 C.
- Plastics and Elastomers End Uses
- Cosmetic Packaging
- Flexible Packaging
- Food Packaging
- Plastics and Elastomers Processing Methods
- Coextrusion
- Extrusion
- Thermoforming
Technical data
Table 1 of 1
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density 23°C | 0.9 | g/cm³ | ISO 1183 |
| Melt Flow Rate (MFR) 230°C/2.16 kg | 3 | g/10-min | ASTM D 1238-13 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Tensile Stress at Break 50-mm/min | 23 | MPa | ISO 527 |
| Tensile Stress at Yield 50-mm/min | 33 | MPa | ISO 527 |
| Tensile Strain at Break 50-mm/min | min. 50 | % | ISO 527 |
| Tensile Strain at Yield 50-mm/min | 12 | % | ISO 527 |
| Heat Deflection Temperature 0.45 MPa Un-annealed | 94 | °c | ISO 75B |
| Vicat Softening Temperature A50 (50°C/h 10N) | 155 | °c | ISO 306 |
| Haze 20um | 0.8 | % | ASTM D 1003 |
| Tensile Modulus 1-mm/min | 1500 | MPa | ISO 527 |
| Izod Notched 23°C | 6.2 | KJ/㎡ | — |