Teldene® H26ML
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Teldene® H26ML is used as injection molding for thin-walled articles, containers, toys, vacuum flasks, household and kitchen articles, components of compounding and master batches application, and suitable for Lamination application.
Properties
- Physical Form
- Granules
- Solid
Product families
- Polyolefins
Other characteristics
- Brand
- Teldene
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 25.0 - 25.0 g/10 min
- Processing Methods
- Injection Molding, Lamination
- Markets
- Consumer Goods
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Special Features
Shows broad processing window while providing good mechanical properties
- Material Features
- Broad Processing Window
- Dimensional Stability
- Food Contact Acceptable
- Good Fluidity
- Good Mechanical Properties
- Good Mold Fillability
- Good Processability
- High Stiffness
- Key Characteristics
High fluidity; High stiffness; Outstanding processability; Easy mold filling; Short cycle times; Good dimensional stability; Food contact approval for specific applications (refer to NATPET)
- Storage and Handling
Polypropylene resin should be stored to prevent a direct exposure to sunlight and heat. The Product estimated shelf life is one year starting from production date, adequate humidity below 80%, and tempera- ture below 40°C. Customers might not fully follow the optimal storage condition, hence the shelf life recommended at customer site is six months only as received.
- Processing Conditions
Average extruder temperature range may be kept between 220- 240°C.
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
- Lamination
Technical data
Table 1 of 1
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density 23°C | 0.9 | g/cm³ | ISO 1183 |
| Melt Flow Rate (MFR) 230°C/2.16 kg | 25 | g/10-min | ASTM D 1238-13 |
| Flexural Modulus | 1500 | MPa | ISO. 178 |
| Tensile Stress at Break 50-mm/min | 23 | MPa | ISO 527 |
| Tensile Stress at Yield 50-mm/min | 32 | MPa | ISO 527 |
| Tensile Strain at Break 50-mm/min | min. 50 | % | ISO 527 |
| Tensile Strain at Yield 50-mm/min | 13 | % | ISO 527 |
| 120 jotehed 23°C | 44 | KJ/㎡ | ISO 180 |
| Heat Deflection Temperature 0.45 MPa Un-annealed | 94 | °¢ | ISO 75B |
| Vicat Softening Temperature A50 (50°C/h 10N) | 152 | °C | ISO 306 |