Teldene® H08CFM
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Teldene® H08CFM is used as extrusion for transparent cast film, shopping bags production. Engaged for packing film of snacks, pasta, bakery items, books, blankets, hosiery, shirts, lamination, automotive compounding.
Properties
- Physical Form
- Granules
- Solid
Product families
- Polyolefins
Other characteristics
- Brand
- Teldene
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 8.0 - 8.0 g/10 min
- Processing Methods
- Coextrusion, Extrusion
- Markets
- Automotive & Transportation
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Calcium Stearate-free
- Food Contact Acceptable
- Food Regulations
This product is defined as a preparation under specific food contact regulation. Detailed information will be provided in a relevant document "Regulatory Compliances Product Declaration" upon request.
- Special Features
Shows broad processing window while providing good mechanical properties
- Material Features
- Broad Processing Window
- Excellent Transparency Properties
- Food Contact Acceptable
- Good Mechanical Properties
- Good Printability
- High Gloss
- Metallizable
- No Anti-blocking Agent
- Key Characteristics
High transparency; High gloss and good printability after corona treatment; No slip or anti-blocking agents; Metallizable, calcium stearate free; Food contact approval for specific applications (refer to NATPET)
- Storage and Handling
Polypropylene resin should be stored to prevent a direct exposure to sunlight and heat. The Product es-timated shelf life is one year starting from production date, adequate humidity below 80%, and tempera-ture below 400 C. Customers might not fully follow the optimal storage condition, hence the shelf life recommended at customer site is six months only as received.
- Processing Conditions
Average extruder temperature range may be kept between 240- 2600 °C.
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Coextrusion
- Extrusion
Technical data
Table 1 of 1
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density 23°C | 0.9 | g/cm³ | ISO 1183 |
| Melt Flow Rate (MFR) 230°C/2.16 kg | 8 | g/10-min | ASTM D 1238-13 |
| Tensile Stress at Break 50-mm/min | 23 | MPa | ISO 527 |
| Tensile Stress at Yield 50-mm/min | 34 | MPa | ISO 527 |
| Tensile Strain at Break 50-mm/min | 650 | % | ISO 527 |
| Tensile Strain at Yield 50-mm/min | 13 | % | ISO 527 |
| IZOd notched 23°C | 46 | KJ/㎡ | ISO 180 |
| Heat Deflection Temperature 0.45 MPa Un-annealed | 90 | °c | ISO 75B |
| Vicat Softening Temperature A50 (50°C/h 10N) | 154 | °C | ISO 306 |
| Haze 100um | max. 1 | % | ASTM D 1003 |
| Gloss 45°; 100um | 87.9 | % | ASTM D 2457 |
| Tensile Modulus 1-mm/min | 1500 | MPa | ISO 527 |