MICOROX® 1295 SEALER
- Chemical Family
- Epoxy & Epoxy Derivatives
MICOROX® 1295 Sealer is a 100% solids, 2 component epoxy sealer designed as a coating for concrete floors and a sealer for other MICOROX® FLOORING SYSTEMS. It is ideal for commercial, institutional, and light manufacturing areas where a high-quality coating or sealer is required. 1295 Sealer offers a durable abrasion resistant surface. It provides excellent resistance to many common industrial chemicals, grease, oil, and cleaning compounds. Excellent handling characteristics provide easy installation using brush, roller, and other common application techniques. 1295 can also be used as a base for colored vinyl flake floors.
Product families
Applications
- Concrete Coatings & Stains
- Floor Coatings
Product Families
- Primers & Sealers
Other characteristics
- Brand
- MICOROX
- Features
- Abrasion Resistant, Chemical Resistant
- Product Type
2K (2 component) Coating, Epoxy Coating, Sealer, Solventless & High Solids Coating; 2K (2 component) Coating; Epoxy Coating; Sealer; Solventless & High Solids Coating
- Application Method
- Brush, Roller
- Compatible Substrates & Surfaces
- Concrete
- Markets
- Building & Construction
- Paints & Coatings
- PACKAGING
1295 Sealer is packaged in 3 and 15 gallon units.
- Application
1295 SEALER is extremely easy to use. It may be installed by plant personnel or local contractors.; On concrete surfaces MICOROX® 103 Primer makes an excellent primer. Apply the primer in a very thin, even film with no build up or puddling. Coat after water and co-solvent have evaporated, usually 6 to 8 hours.; Mix 1295 SEALER by combining one container of resin with one container of hardener. Mix thoroughly with a drill-stirrer.; Premix components to redisperse any settled fillers or pigments. Materials should be mixed for approximately two minutes. No induction time is required. The material may be applied immediately.; Note: 15 gallon batches require field measurement. Mixing ratio is 2 resin to 1 hardener by volume.; Apply the material by squeegee, roller or brush.; Apply in a thin, even film of 8-10 mils thickness; If a second coat is being applied, timing iscritical. Allow the first coat to harden. Additional coats should be applied within 24 hours of the initial application.
- Precaution
Contact with liquids Part A and B can cause irritation. Wear protective clothing. Cover hands with protective cream and/or gloves. Wear chemical splash goggles. Use only with adequate ventilation.
- Availability
Available in Clear and 14 basic colors. Custom colors upon request.
- Technology
- Ready-to-Use Products
- Application Methods
- Brush
- Roller
- Hardening and Cure
1295 SEALER hardens for foot traffic in 12 hours at 77°F Complete cure may require 24 to 72 72 hours depending on temperature and humidity.; Cure Rate: Allow (at 77°F (25°C); 12 hours for foot traliic; 18 hours for light traffic; 24 hours for normal operations
- HIGHLIGHTS
MICOROX® 1295 SEALER is a two component 100% solids epoxy sealer designed to offer a high gloss durable coating for concrete and other surfaces.
- Surface Preparation
When used as a topcoat for micorox flooring systems: To remove trowel marks and present an even, level surface for 1295 SEALER, use a floor grinder with medium stones and vacuum resulting dust before applying 1295 Sealer.. When applied as a concrete floor sealer, 1295 SEALER bonds to most existing surfaces with an appropriate primer. Substrate must be exposed by acid-etch or mechanical means for secure bonding. See installation instructions for further details.
- Application Areas
Commercial, institutional, and light industrial floors. Manufacturing and food service areas. As a binder for colored vinyl flake floors.
- Temperature Limitations
During the installation and cure of 1295 SEALER, surface temperatures of 60° F - 90°F are recommended. Do not apply urethane top coat if substrate temperature is below 60° F.
- Ready to Use Product Features
- Abrasion Resistant
- Chemical Resistant
- Compatible Substrates and Surfaces
- Concrete
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compressive Strength | 10100.0 | psi | ASTMD-695-77 |
| Compressive Modulus | 1.95 x 10⁵ | psi | ASTMD-695-77 |
| Tensile Strength | 7100.0 | psi | ASTM D638-77a |
| Tensile Modulus | 3.6 x 10⁴ | psi | ASTM D-638-77a |
| Tensile Elongation | 10.7 | % | ASTM D 638-77a |
| Flexural Strength | 12500.0 | psi | ASTM D-790-71 |
| Flexural Modulus | 3.7 X 10⁵ | psi | ASTM D-790-71 |
| Hardness | 80 - 85 | Shore D | ASTM D-2240/Durometer |
| Bond Strength (100% Concrete Failure) | max. 400 | psi | — |
| Abrasion Resistance | 0.04 | gm /1000 revolutions | ASTM D-4060, Taber Abrader, 5-17 wheel, 1,000 gm load |
| Flammability | max. 0.25 | inches | ASTM D-635 |
| Water Absorption | 0.1 | % | ASTM C-413 |