MICOROX® 23-33F FAST PRIMER
- Chemical Family
- Epoxy & Epoxy Derivatives
Micorox® 23-33F Fast Primer is 100% solids, 2-part epoxy floor primer/ sealer. It features extremely rapid thin films set even at reduced temperatures. In addition to rapid cure, it provides excellent adhesion and resistance to a wide variety of chemicals.
Product families
Applications
- Primers & Lacquers
Product Families
- Primers & Sealers
Other characteristics
- Brand
- MICOROX
- Features
Chemical Resistant, Good Adhesion, Rapid Curing Speed; Outstanding adhesion; Deep penetration; Rapid cure
- Product Type
2K (2 component) Coating, Epoxy Coating, Primer, Sealer, Solventless & High Solids Coating; 2K (2 component) Coating; Epoxy Coating; Primer; Sealer; Solventless & High Solids Coating
- Markets
- Printing & Packaging
- PACKAGING
23-33 Primer/Sealer is packaged in preproportioned 1 gallon units.
- Application
- Mix Micorox® 23-33 by combining the entire contents of the Hardener container with that of entire contents of the Resin container. The material should be mixed with a drill and mixing paddle for 2 minutes. The extremely rapid set time of the 23-33 requires immediate application after mixing. The material should be poured onto the surface to be coated then spread with a brush or roller.
- Working Life
- 15-20 Minutes once spread on the floor. (If the material is left in the can, it will gel more rapidly)
- Clean Up
- Clean up tools immediately after use with hot, soapy water and abrasive pads.
- Precaution
Wear protective clothing. Cover hands with vinyl or neoprene gloves. Wear chemical splash goggles. Use only with adequate ventilation.
- Technology
- Ready-to-Use Products
- Hardening and Cure
Micorox® 23-33 hardens for foot traffic in 2.5-3.0 hours at 77°F. Complete cure may require 18-72 hours depending upon temperature.
- HIGHLIGHTS
MICOROX® 23-33 is a rapid setting 2 component epoxy primer/sealer used to improve the adhesion of Micorox flooring systems. The primers extremely rapid thin film set time, even at low temperatures, can result in substantial time savings during the priming phase of floor installation.
- Surface Preparation
Surface to be coated should be clean and free from oil, grease, wax or any foreign substance. Concrete surfaces should be prepared by mechanical means and/or acid etching.
- Temperature Limitations
During the installation and cure, surface temperatures of 60°F-80°Fare recommended. 23-33 may be applied at lower temperatures.
- Ready to Use Product Features
- Chemical Resistant
- Good Adhesion
- Rapid Curing Speed
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density Resin | 9.26 | Ibs/gal | — |
| Density Hardener | 8.88 | Ibs/gal | — |
| Mixed Density | 9.16 | lb/gal | — |
| Mixing Ratio (Resin to Hardner by Weight) | 100 to 32 | — | — |
| Mixing Ratio (Resin to Hardner by Volume) | 3 to 1 | — | — |
| Pot Life (77°F) | 9 | minutes | — |
| Thin Film Set Time | 2.5 - 3.0 | hours | — |
| Tensile Strength | 10000.0 | psi | ASTM D638 |
| Elongation | 5.0 | % | ASTM D638 |
| Hardness | 85 - 89 | Shore D | ASTM D-2240/Durometer |
| Bond Strength | 400.0 | psi | — |