Extrudr Flex Semisoft black
- Chemical Family
- Polycaprolactone (PCL)Polyesters
Extrudr Flex Semisoft black is a durable elastomere based on Polycaprolacton-Polyester. It was specially developed for industrial applications and is ideally suited for the production of elastic and damping components. The material is optimized for the FFF/FDM process in regards to thermal stability and better flow properties. The raw material is compliant according to the REACH- and RoHS-Standards.
Properties
- Physical Form
- Filament
Product families
Applications
Applications
- Consumer Goods — Housewares; Consumer Goods — Other Consumer Goods Applications; Consumer Goods — Sports & Recreation
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Tooling & Moldmaking
Product Families
Plastics — 3D Printing Polymers
- Thermoplastic Filament
Other characteristics
- Density
- 1180.0 - 1180.0 kg/m³
- End Uses
3D Printing Applications, Consumer Applications, Industrial Parts, Prototyping, Toys
- Polymer Name
- Polycaprolactone (PCL), Thermoplastic Polyester
- Polycaprolactone (PCL)
- Thermoplastic Polyester
- Processing Methods
- Fused Filament Fabrication
- Color
- Black
- Markets
- Consumer Goods
- Industrial
- Features
- Good mechanical properties
- Excellent chemical resistance
- Free of silicone, softeners and oil
- Free of halogen
- UV-Resistant
- Technology
- Plastics
- Labeling Claims
- Halogen-free
- Silicone-free
- Material Features
- Chemical Resistant
- Excellent Flow Properties
- Good Adhesion
- Good Bonding Strength
- Good Elongation
- Good Impact Strength
- Good Mechanical Properties
- Good Printability
- Shelf Life Storage
Store in a dry room at room temperature (18-27°C / 65-80°F). Keep out of direct heat and sunlight. When stored correctly, this material has a shelf life of 2 years.
- Certifications and Compliance
- FDA Compliant
- REACH (Europe)
- RoHS Compliant
- Plastics and Elastomers End Uses
- 3D Printing Applications
- Consumer Applications
- Industrial Parts
- Prototyping
- Toys
- Plastics and Elastomers Processing Methods
- Fused Filament Fabrication
Technical data
Table 1 of 1
17 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness | 88 | Shore A | ISO 868 |
| Tensile Modulus (E-Modulus) | 42 | MPa | ISO 527-2/5A/500 |
| Ultimate Elongation | 550 | % | ISO 527-2/5A/500 |
| Stress At Break (50%) | 9 | MPa | ISO 527-2/5A/500 |
| Stress At Break (100%) | 11 | MPa | ISO 527-2/5A/500 |
| Stress At Break (300%) | 22 | MPa | ISO 527-2/5A/500 |
| Vicat A (Vst) | 98* | °C | ISO 306 |
| Melting Temperature | 180-230 | °C | ISO 3146-C |
| Density | 1.18 | g/cm³ | ISO 2781 |
| Abrasion Resistance | 25 | mm³ | ISO 4649-A |
| Tear Strength Unnicked | 135 | kN/m | ISO 34-1B |
| Glass Transition Temperature | 34 | °C | — |