Extrudr Wood Brown

Chemical Family: PolyestersPolylactic Acid (PLA)

Extrudr Wood Brown is made from renewable resources like lignin and other biopolymers. This wood-fiber reinforced plastic boasts extraordinary processing properties. In addition, the raw material is approved according to the REACH-, RoHS- and FDA-Standards.

Properties

Physical Form: Filament

Product families

Applications

Consumer Goods — Housewares; Consumer Goods — Other Consumer Goods Applications; Consumer Goods — Sports & Recreation

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts
Tooling & Moldmaking

Product Families

Plastics — 3D Printing Polymers

Thermoplastic Filament

Other characteristics

Density: 1300.0 - 1300.0 kg/m³
End Uses: 3D Printing Applications, Consumer Applications, Industrial Parts, Prototyping, Toys
Polymer Name: Polylactic Acid (PLA)
Flexural Modulus: 3200.0 - 3200.0 MPa
Processing Methods: 3D Printing
Markets: Consumer Goods
Industrial
Features: Good printing and flow properties
Wood-like smell and esthetic
Low warping tendency
Biodegradable (DIN EN ISO 14855)
Technology: Plastics
Labeling Claims: Biodegradable
From Renewable Resources
Silicone-free
Fillers Included: Natural Fiber
Material Features: Biodegradable
Excellent Flow Properties
Good Adhesion
Good Aesthetics
Good Elongation
Good Impact Strength
Good Printability
Good Processability
Shelf Life Storage: Store in a dry room at room temperature (18-27°C / 65-80°F). Keep out of direct heat and sunlight. When stored correctly, this material has a shelf life of 2 years.
Certifications and Compliance: FDA Compliant
REACH (Europe)
RoHS Compliant
Plastics and Elastomers End Uses: 3D Printing Applications
Consumer Applications
Industrial Parts
Prototyping
Toys
Plastics and Elastomers Processing Methods: 3D Printing

Technical data

Table 1 of 1

8 rows

Characteristic	Value	Unit	Method
Density	1.3	g/cm³	ISO 1183
Density	1.23	g/cm³	ISO 2781
Flexural Modulus	3200	MPa	ISO 527
Tensile Strength	40	MPa	ISO 527
Breaking Stress	2	%	ISO 527
Flexural Strength	43	MPa	ISO 527
MFR	22	g/10min	ISO 1133
Vicat A (Vst)	48*	°C	ISO 306