To catalogue
Extrudr Flax beige
- Chemical Family
- PolyestersPolylactic Acid (PLA)
Extrudr Flax beige is made from renewable resources and it allows fast productionspeed thanks to added mineral filler. The material is developed for rapid prototyping applications. At high temperatures and regular printing speed, the surface becomes coarse and resembles sandstone. The raw material is approved according to the REACH-, RoHS- and FDA-Standards.
Properties
- Physical Form
- Filament
Product families
Applications
Applications
- Consumer Goods — Housewares; Consumer Goods — Other Consumer Goods Applications; Consumer Goods — Sports & Recreation
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Tooling & Moldmaking
Product Families
Plastics — 3D Printing Polymers
- Thermoplastic Filament
Other characteristics
- Density
- 1450.0 - 1450.0 kg/m³
- End Uses
3D Printing Applications, Consumer Applications, Industrial Parts, Prototyping, Toys
- Polymer Name
- Polylactic Acid (PLA)
- Flexural Modulus
- 3400.0 - 3400.0 MPa
- Processing Methods
- 3D Printing
- Color
- Beige
- Markets
- Consumer Goods
- Industrial
- Features
- Very good printing and flow properties
- Mineral-like smooth surface
- Low warping tendency
- Biodegradable (DIN EN ISO 14855)
- Technology
- Plastics
- Labeling Claims
- Biodegradable
- From Renewable Resources
- Silicone-free
- Fillers Included
- Mineral
- Material Features
- Biodegradable
- Excellent Flow Properties
- Good Adhesion
- Good Elongation
- Good Printability
- Good Smoothness
- High Temperature Resistance
- Impact Resistance
- Shelf Life Storage
Store in a dry room at room temperature (18-27°C / 65-80°F). Keep out of direct heat and sunlight. When stored correctly, this material has a shelf life of 2 years.
- Certifications and Compliance
- FDA Compliant
- REACH (Europe)
- RoHS Compliant
- Plastics and Elastomers End Uses
- 3D Printing Applications
- Consumer Applications
- Industrial Parts
- Prototyping
- Toys
- Plastics and Elastomers Processing Methods
- 3D Printing
Technical data
Table 1 of 1
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 3400 | MPa | ISO 527 |
| Tensile Strength | 43 | MPa | ISO 527 |
| Breaking Stress | 3 | % | ISO 527 |
| Elongation At Break | 22.3 | % | ISO 527 |
| Flexural Strength | 30 | MPa | ISO 527 |
| MFR | 15 | g/10min | ISO 1133 |
| Vicat A (Vst) | 48* | °C | ISO 306 |
| Density | 1.45 | g/cm³ | ISO 2781 |