Extrudr PLA NX2 Purple
- Chemical Family
- PolyestersPolylactic Acid (PLA)
Extrudr PLA NX2 Purple is made form a renewable biopolymer. It combines good mechanical properties with high flexibility. It is suitable for industrial use, rapid prototyping, architecture, food-applications, etc. The raw material is approved according to the REACH-, RoHS- and FDA- Standards.
Properties
- Physical Form
- Filament
Product families
Plastics — 3D Printing Polymers
- Thermoplastic Filament
Other characteristics
- End Uses
3D Printing Applications, Consumer Applications, Food Packaging, Industrial Parts, Prototyping, Toys
- Polymer Name
- Polylactic Acid (PLA)
- Flexural Modulus
- 2650.0 - 2650.0 MPa
- Processing Methods
- 3D Printing
- Color
- Purple
- Markets
- Consumer Goods
- Industrial
- Printing & Packaging
- Features
- Smooth matte finish
- Safety-of-Toys" Compliant
- Optimized impact strength
- Low warping tendency
- Biodegradable (EN 13432)
- Technology
- Plastics
- Labeling Claims
- Biodegradable
- From Renewable Resources
- Silicone-free
- Material Features
- Biodegradable
- Good Adhesion
- Good Elongation
- Good Impact Strength
- Good Mechanical Properties
- Good Printability
- High Flexibility
- High Temperature Resistance
- Shelf Life Storage
Store in a dry room at room temperature (18-27°C / 65-80°F). Keep out ofdirect heat and sunlight. When stored correctly, this material has a shelf life of 2 years
- Certifications and Compliance
- FDA Compliant
- REACH (Europe)
- RoHS Compliant
- Plastics and Elastomers End Uses
- 3D Printing Applications
- Consumer Applications
- Food Packaging
- Industrial Parts
- Prototyping
- Toys
- Plastics and Elastomers Processing Methods
- 3D Printing
Technical data
Table 1 of 1
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (E-Modulus) | 2650 | MPa | ISO 178 |
| Tensile Modulus (E-Modulus) | 2600 | MPa | ISO 527 |
| Tensile Strength | 47 | MPa | ISO 527 |
| Elongation At Strength | 4 | % | ISO 527 |
| Stress At Break | 23 | MPa | ISO 527 |
| Nominal Elongation At Break | 19 | % | ISO 527-2 |
| Notched Impact Strength | 7 | kj/m² | ISO 179/1eA |
| Unnotched Impact Strength | no break | kj/m² | ISO 179/1eU |
| Vicat A (Vst) | 60* | °C | ISO 306 |
| Melting Temperature | 180-200 | °C | ISO 3146-C |
| MFR | 5 | g/10min | ISO 1133 |
| Shrinking | 0.3 | % | ISO 294-4 |