Extrudr Pearl Nature
- Chemical Family
- PolyestersPolylactic Acid (PLA)
Extrudr Pearl Nature is made from renewable resources and is developed for rapidprototyping applications. The material offers excellent tensile stretch properties. The raw material is approved according to the REACH-, RoHS- and FDAStandards.
Properties
- Physical Form
- Filament
Product families
Applications
Applications
- Consumer Goods — Housewares; Consumer Goods — Other Consumer Goods Applications; Consumer Goods — Sports & Recreation
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Tooling & Moldmaking
Product Families
Plastics — 3D Printing Polymers
- Thermoplastic Filament
Other characteristics
- Density
- 1250.0 - 1250.0 kg/m³
- End Uses
3D Printing Applications, Consumer Applications, Industrial Parts, Prototyping, Toys
- Polymer Name
- Polylactic Acid (PLA)
- Flexural Modulus
- 2500.0 - 2500.0 MPa
- Processing Methods
- 3D Printing
- Color
- Beige
- Markets
- Consumer Goods
- Industrial
- Features
- Very good printing and flow properties
- uniquely smooth surface
- Low warping tendency
- Biodegradable (DIN EN ISO 14855)
- Technology
- Plastics
- Labeling Claims
- Biodegradable
- Silicone-free
- Material Features
- Biodegradable
- Excellent Flow Properties
- Excellent Tensile Properties
- Good Adhesion
- Good Elongation
- Good Impact Strength
- Good Printability
- High Temperature Resistance
- Shelf Life Storage
Store in a dry room at room temperature (18-27°C / 65-80°F). Keep out of direct heat and sunlight. When stored correctly, this material has a shelf life of 2 years.
- Certifications and Compliance
- FDA Compliant
- REACH (Europe)
- RoHS Compliant
- Plastics and Elastomers End Uses
- 3D Printing Applications
- Consumer Applications
- Industrial Parts
- Prototyping
- Toys
- Plastics and Elastomers Processing Methods
- 3D Printing
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2500 | MPa | ISO 527 |
| Tensile Strength | 34 | MPa | ISO 527 |
| Breaking Stress | 3 | % | ISO 527 |
| Elongation At Break | 6.9 | % | ISO 527 |
| E-Modulus | 1800 | MPa | ISO 178 |
| Flexural Strength | 30.1 | MPa | ISO 527 |
| MFR | 4 | g/10min | ISO 1133 |
| Vicat A (Vst) | 58* | °C | ISO 306 |
| Hdt/B | 51 | °C | ISO 75 |
| Shrinking | 0.67 | % | ISO 294-4 |
| Density | 1.25 | g/cm³ | ISO 2781 |