FLUORONOID® FL 110
- Chemical Family
- Fluoropolymers
FLUORONOID® FL 110 is a Bronze filled PTFE
Product families
Applications
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- FLUORONOID
- Polymer Name
- Polytetrafluoroethylene (PTFE)
- Fillers Included
- Bronze
- Markets
- Automotive & Transportation
- Formulations
- 60% PTFE, 40% BRONZE POWDER (BY WEIGHT)
- Technology
- Plastics
- Material Features
Dimensional Stability; Electrically Conductive; Excellent Dielectric Properties; Good Compressive Strength; Good Environmental Stress Crack Resistance (ESCR); Good Thermal Conductivity; High Hardness; Low Creep; Low Flow; Low Wear; Non Stick; Superior Coefficient of Friction; Temperature Resistance
- HIGHLIGHTS
Addition of bronze to PTFE increases hardness and compressive strength, provides better dimensional stability and lowers creep, cold flow and wear. It also increases thermal and electrical conductivity.
- Certifications and Compliance
- ISO 14001
- ISO 9001
- TÜV Approved
- Plastics and Elastomers End Uses
- Aerospace Applications
- Bearing Bushes
- Bearings
- Gaskets
- O Rings
- Pipe Seals
- Seats
- Tubes
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 1
17 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compressive Strength (at 0.2% offset, Moulding Direction) | 9.7 | Mpa | — |
| Compressive Strength (at 0.2% offset, Cross Direction) | 9.0 | Mpa | — |
| Permanent Deformation (Moulding Direction) | 4.4 | % | — |
| Permanent Deformation (Cross Direction) | 3.1 | % | — |
| Deformation Under Load (24 hours, 6.9 MPa, 23ºC, Moulding Direction) | 8.6 | % | — |
| Deformation Under Load (24 hours, 6.9 MPa, 23ºC,Cross Direction) | 7.0 | % | — |
| Coefficient of Thermal Expansion (25 - 150ºC (cm/cm/ºC), Moulding Direction) | 1.17×10^(-4) | — | — |
| Coefficient of Thermal Expansion (25 - 150ºC (cm/cm/ºC), Cross Direction) | 1.08×10^(-4) | — | — |
| Specific Gravity | 3 ± 3.2 | — | BS EN ISO 13000-2 |
| Tensile Strength | min. 19 | Mpa | BS EN ISO 13000-2 |
| Elongation | min. 230 | % | BS EN ISO 13000-2 |
| Hardness | 63 - 68 | Shore D | BS EN ISO 13000-2 |