FLUORONOID® FL 115
- Chemical Family
- Fluoropolymers
FLUORONOID® FL 115 is a Carbon filled PTFE. Carbon filler gives good compression and wear resistance, good thermal conductivity and low permeability.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Industrial — Oil, Gas & Mining
- Other Oil Gas & Mining Applications
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- FLUORONOID
- Polymer Name
- Polytetrafluoroethylene (PTFE)
- Fillers Included
- Carbon Fiber
- Markets
- Industrial
- Formulations
- 75% PTFE, 25% CARBON (BY WEIGHT)
- Technology
- Plastics
- Material Features
- Excellent Dielectric Properties
- Good Compression Set
- Good Compressive Strength
- Good Thermal Conductivity
- High Hardness
- Low Permeability
- Low Thermal Expansion
- Temperature Resistance
- Typical Applications
- FL 115 is used in sealing applications.
- Certifications and Compliance
- ISO 14001
- ISO 9001
- TÜV Approved
- Plastics and Elastomers End Uses
- Bearings
- Gaskets
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 2.05 - 2.12 | — | BS EN ISO 13000-2 |
| Tensile Strength | min. 11 | Mpa | BS EN ISO 13000-2 |
| Elongation | min. 70 | % | BS EN ISO 13000-2 |
| Hardness | 60 - 75 | Shore D | BS EN ISO 13000-2 |
| Maximum Working Temperature | 260.0 | °C | BS EN ISO 13000-2 |
| Compressive Strength (at 0.2% offset, axial) | 16.5 | Mpa | ASTM D695 |
| Deformation Under Load (24 Hours, 2000 psi total) | 2.0 | % | ASTM D621 |
| Deformation Under Load (24 Hours, 2000 psi permanent) | 1.0 | % | ASTM D621 |
| Water Absorption | max. 0.2 | % | ASTM D570 |
| Thermal Conductivity | 0.59 | W/(m·K) | — |
| Coefficient of Thermal Expansion (||) | 15×10^(-5) | /°C | BS EN ISO 13000-2 |
| Volume Resistivity | 10^4 | Ω-Cm | — |