DAP D62/6130F
- Chemical Family
- OrthophthalicsPhthalatesUnsaturated Polyester (UPE)
DAP D62/6130F is a versatile diallyl ortho-phthalate molding compound, with the added benefits of being flame retardant and long-glass fiber filled. It is supplied in flake form, making it convenient for various applications. This compound can be efficiently molded using compression or transfer equipment and is easily preformed for ease of handling. Notably, it maintains its performance when stored at room temperature for up to one year. Additionally, it has successfully passed NASA outgassing tests, indicating its suitability for a range of applications, including those with stringent requirements.
Properties
- Physical Form
- Flakes
- Solid
Product families
Applications
- Housings & Enclosures
- Terminal Blocks Plugs & Sockets
Product Families
- Other Thermoset Resins
Other characteristics
- Brand
- DAP
- Density
- 1820.0 - 1820.0 kg/m³
- End Uses
Housings, Insulators, Structural Parts, Terminal Blocks
- Polymer Name
- Diallyl Phthalate
- Tensile Strength
- 0.0414 - 69.0 MPa
- Processing Methods
- Compression Molding, Transfer Molding
- Markets
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- Key Features
D62 / 6130F is particularly suited to applications requiring resistance to elevated temperatures and high humidity.. It has a high impact strength, excellent compressive and flexural strength, and very good electrical properties.
- Technology
- Plastics
- Fillers Included
- Glass Fiber
- Long Glass Fiber
- Additives Included
- Flame Retardant
- Material Features
- Easy To Mold
- Flame Retardant
- General Purpose
- Good Compressive Strength
- Good Electrical Properties
- Good Flexural Modulus
- Good Impact Strength
- High Strength
- Applications
Structural parts, housings, terminals, insulators and other applications requiring flame resistance or strength.
- Certifications and Compliance
- ISO 9001
- UL 94
- Plastics and Elastomers End Uses
- Housings
- Insulators
- Structural Parts
- Terminal Blocks
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Compression Molding
- Transfer Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Flexural Strength | 13 - 17,000 | psi |
| Compressive Strength | 24 - 30,000 | psi |
| Tensile Strength | 6 - 10,000 | psi |
| Impact Strength (Izod Notched) | 3.0 - 6.0 | ft-lb / inch |
Table 2 of 5
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Dimensional Stability | max. 0.01 | % |
| Thermal Expansion (at -40 °C to 100 °C) | 2.4 | 10⁻⁵ / °C |
| Heat Distortion Temperature (at 18.6 kg/cm²) | 260 | °C |
Table 3 of 5
16 rows| Characteristic | Value | Unit |
|---|---|---|
| Arc Resistance | 180 | seconds |
| Dielectric Strength (Kv Step-by-Step, Dry) | 400 | volts/mil |
| Dielectric Strength (Kv Step-by-Step, Wet) | 360 | volts/mil |
| Dielectric Breakdown (Step-by-Step, Dry) | 62 | Kv |
| Dielectric Breakdown (Step-by-Step, Wet) | 60 | Kv |
| Dielectric Constant (at 1 KHz, Dry) | 4.2 | — |
| Dielectric Constant (at 1 KHz, Wet) | 4.4 | — |
| Dissipation Factor (at 1KHz, Dry) | 0.006 | — |
| Dissipation Factor (at 1KHz, Wet) | 0.009 | — |
| Surface Resistance Megaohms (As is) | min. 10¹⁰ | — |
| Surface Resistance, megaohms (at 70 °C, 30 Days, at 100% RH) | 20000 | — |
| Surface Resistance, megaohms (at 70 °C, 30 Days, at 100% RH) | 26000 | — |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Water Absorption (at 50 °C,48 hours) | 0.3 | % |
| Water Extract Conductance | 30 x 10⁻⁶ | Mhos / cm |
Table 5 of 5
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity | 1.82 | — |
| Bulk Factor | 6 | — |
| Molding Pressure | 500 - 8,000 | psi |
| Molding Temperature | 135 - 190 | °C |
| Mold Shrinkage | 0.001 - 0.004 | In / In |