Formac Black Formamid 6
- Chemical Family
- Polyamides
Formac Black Formamid 6 is an injection molding grade is used for automotive & farming mechanics, consumer goods and industrial applications. It has good stiffness, wear resistance and toughness.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Lawn & Garden; Consumer Goods — Other Consumer Goods Applications; Consumer Goods — Sports & Recreation
Automotive & Transportation — Automotive
- Interior
- Other Automotive Applications
- Powertrain & UTH
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Formamid
- Polymer Name
- Polyamide 6 (PA 6)
- Flexural Modulus
- 2900.0 - 2900.0 MPa
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Automotive & Transportation
- Consumer Goods
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Material Features
- Good Stiffness
- Good Toughness
- Wear Resistant
- Certifications and Compliance
- ISO 9001
- UL 94
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Automotive Under The Hood
- Consumer Applications
- Doors
- Industrial Parts
- Sporting Goods
- Windows
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Point (DSC) | 222.0 | °C | ISO 3146 |
Table 2 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 3100.0 | MPa | ISO 527 - 2 |
| Stress at Break | 85.0 | MPa | ISO 527 - 2 |
| Strain at Break | 8.0 | % | ISO 527 - 2 |
| Flexural Modulus | 2900.0 | MPa | ISO 178 |
| Maximum Flexural Stress | 100.0 | MPa | ISO 178 |
| IZOD Notched Impact Strength (+23°C) | 4.5 – 5.5 | KJ/m2 | ISO 180/1eA |
Table 3 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Distortion Temperature (Under 1.8 Mpa Load, HDT A) | 65.0 | °C | ISO 75 - 2 |
| Heat Distortion Temperature (Under 0.45 MPa Load, HDT B) | 180.0 | °C | ISO 75 - 2 |
| Vicat Softening Point (Under 0.49 N Load, Vicat B) | 192.0 | °C | ISO 306 |
Table 4 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | 10000000000000.0 | Ω*cm | IEC 60093 |
| Surface Resistivity | 100000000000000.0 | Ω | IEC 60093 |
| Comparative Tracking Index | 60.0 | V | IEC 60112 |
Table 5 of 7
3 rows| Characteristic | Value | Method |
|---|---|---|
| Flammability Rate (0.8 mm thickness) | HB | UL94 |
| Flammability Rate (1.6 mm thickness) | HB | UL94 |
| Flammability Rate (3.2 mm thickness) | HB | UL94 |
Table 6 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Temperature | 245 - 280 | °C | CYLINDER |
| Melt Mold | 70 -80 | °C | MOLD |
| Drying Temperature | 80.0 | °C | — |
| Dry Time | 4.0 | h | — |
Table 7 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.14 | g/cm3 | ISO 1183 |
| Humidity Absorption | 3.0 | % | Similar ISO 62 |
| Water Absorption (23°C 50% r.U) | 8.0 | % | ISO 62 |
| Melt Volume-Flow Rate (275°C 5kg) | 100.0 | °C | ISO 1133 |
| Molding Shrinkage (Parallel) | 0.9 - 1 | % | ISO 294-4 |
| Molding Shrinkage (Normal) | 1 - 1.2 | % | ISO 294-4 |