Formalen PP-Copolymer 30% glass fibre reinforced Black
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Formalen PP-Copolymer 30% glass fiber reinforced Black is used for mechanical, aeronautical, electric and construction applications. It has good stiffness, good resistance to chemicals and good electrical properties.
Product families
Applications
Building & Construction — Building Materials
- Other Building Materials
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Electrical & Electronics — Parts & Components
- Other Parts & Components
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Formalen
- Polymer Name
- Polypropylene Copolymer
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Material Features
- Chemical Resistant
- Chemically Coupled
- Good Electrical Properties
- Good Stiffness
- Certifications and Compliance
- ISO 9001
- UL 94
- Plastics and Elastomers End Uses
- Aerospace Applications
- Construction Applications
- Electrical Parts
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Point (DSC) | 165.0 | °C | ISO 3146 |
| Tensile Modulus | 4800.0 | MPa | ISO 527 - 2 |
| Tensile Stress Yield | 69.0 | MPa | ISO 527 - 2 |
| Strain at Break | 2.9 | % | ISO 527 - 2 |
| Flexural Modulus | 4500.0 | MPa | ISO 178 |
| Maximum Flexural Stress | 113.0 | MPa | ISO 178 |
| IZOD Notched Impact Strength (+23°C) | 14.0 | KJ/m2 | ISO 180/1eA |
Table 2 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Distortion Temperature (Under 1.8 Mpa Load, HDT A) | 138.0 | °C | ISO 75 - 2 |
| Vicat Softening Point (Under 0.49 N Load, Vicat B) | 117.0 | °C | ISO 306 |
Table 3 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | 1.0e+15 | Ω*cm | IEC 60093 |
| Surface Resistivity | 1.0e+16 | Ω | IEC 60093 |
| Comparative Tracking Index | 600.0 | V | IEC 60112 |
Table 4 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability Rate (0.8 mm thickness) | HB | — | UL94 |
| Flammability Rate (1.6 mm thickness) | HB | — | UL94 |
| Flammability Rate (3.2 mm thickness) | HB | — | UL94 |
| Oxygen Index | 21.0 | % | ISO 4589-1/-2 |
Table 5 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Temperature | 210 - 250 | °C | CYLINDER |
| Melt Mold | 45 - 70 | °C | MOLD |
| Drying Temperature | 80.0 | °C | — |
| Dry Time | 2.0 | h | — |
Table 6 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.13 | g/cm3 | ISO 1183 |
| Humidity Absorption | 0.04 | % | Similar ISO 62 |
| Melt Volume-Flow Rate (230°C 2.16kg) | 9.0 | °C | ISO 1133 |
| Molding Shrinkage (Parallel) | 0.25 - 0.4 | % | ISO 294-4 |
| Molding Shrinkage (Normal) | 0.7 - 0.9 | % | ISO 294-4 |