Formalen PP-Homopolymer 30% glass fibre reinforced Black

Chemical Family: PolyolefinsPolypropylenes (PP)

Formalen PP-Homopolymer 30% glass fiber reinforced Black, injection molding grade is used for mechanical, aeronautical, electric and construction applications. It has good stiffness, good resistance to chemicals, and good electrical properties.

Product families

Applications

Building & Construction — Building Materials

Other Building Materials

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Parts & Components

Other Parts & Components

Automotive & Transportation — Transportation

Aerospace & Aviation

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Brand: Formalen
Polymer Name: Polypropylene Homopolymer (HPP)
Melt Flow Index: 4.0 - 7.0 g/10 min
Fillers Included: Glass Fiber
Processing Methods: Injection Molding
Color: Black
Markets: Automotive & Transportation
Building & Construction
Electrical & Electronics
Industrial
Flame Rating: UL 94 HB
Technology: Plastics
Material Features: Chemical Resistant
Good Electrical Properties
Good Stiffness
Certifications and Compliance: ISO 9001
UL 94
Plastics and Elastomers End Uses: Aerospace Applications
Construction Applications
Electrical Parts
Machine/Mechanical Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

6 rows

Characteristic	Value	Unit	Method
Tensile Modulus	5000 - 5800	MPa	ISO 527 - 2
Stress at Break	75.0	MPa	ISO 527 - 2
Strain at Break	2.5	%	ISO 527 - 2
Flexural Modulus	4800 - 5200	MPa	ISO 178
Maximum Flexural Stress	120.0	MPa	ISO 178
IZOD Notched Impact Strength (+23°C)	9.0	KJ/m2	ISO 180/1eA

Table 2 of 6

2 rows

Characteristic	Value	Unit	Method
Heat Distortion Temperature (Under 1.8 Mpa Load, HDT A)	145.0	°C	ISO 75 - 2
Vicat Softening Point (Under 0.49 N Load, Vicat B)	130.0	°C	ISO 306

Table 3 of 6

2 rows

Characteristic	Value	Unit	Method
Volume Resistivity	100000000000000.0	Ω*cm	IEC 60093
Surface Resistivity	1.0e+15	Ω	IEC 60093

Table 4 of 6

3 rows

Characteristic	Value	Method
Flammability Rate (0.8 mm thickness)	HB	UL94
Flammability Rate (1.6 mm thickness)	HB	UL94
Flammability Rate (3.2 mm thickness)	HB	UL94

Table 5 of 6

4 rows

Characteristic	Value	Unit	Method
Melt Temperature	210-255	°C	CYLINDER
Mould Temperature	45-70	°C	MOULD
Drying Temperature	80.0	°C	—
Dry Time	2.0	h	—

Table 6 of 6