Formalen PP-Homopolymer 30% glass fibre reinforced Natural

Chemical Family: PolyolefinsPolypropylenes (PP)

Formalen PP-Homopolymer 30% glass fiber reinforced Natural is used for mechanical, aeronautical, electric and construction applications. It has good stiffness, good resistance to chemicals, and good electrical properties.

Product families

Applications

Building & Construction — Building Materials

Other Building Materials

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Parts & Components

Other Parts & Components

Automotive & Transportation — Transportation

Aerospace & Aviation

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Brand: Formalen
Polymer Name: Polypropylene Homopolymer (HPP)
Melt Flow Index: 4.0 - 7.0 g/10 min
Fillers Included: Glass Fiber
Processing Methods: Injection Molding
Color: Natural
Markets: Automotive & Transportation
Building & Construction
Electrical & Electronics
Industrial
Flame Rating: UL 94 HB
Technology: Plastics
Material Features: Chemical Resistant
Good Electrical Properties
Good Stiffness
Certifications and Compliance: ISO 9001
UL 94
Plastics and Elastomers End Uses: Aerospace Applications
Construction Applications
Electrical Parts
Machine/Mechanical Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

6 rows

Characteristic	Value	Unit	Method
Tensile Modulus	5000 - 5800	MPa	ISO 527 - 2
Stress at Break	75.0	MPa	ISO 527 - 2
Strain at Break	2.5	%	ISO 527 - 2
Flexural Modulus	4800 - 5200	MPa	ISO 178
Maximum Flexural Stress	120.0	MPa	ISO 178
IZOD Notched Impact Strength (+23°C)	9.0	KJ/m2	ISO 180/1eA

Table 2 of 6

2 rows

Characteristic	Value	Unit	Method
Heat Distortion Temperature (Under 1.8 Mpa Load, HDT A)	145.0	°C	ISO 75 - 2
Vicat Softening Point (Under 0.49 N Load, Vicat B)	130.0	°C	ISO 306

Table 3 of 6

2 rows

Characteristic	Value	Unit	Method
Volume Resistivity	100000000000000.0	Ω*cm	IEC 60093
Surface Resistivity	1.0e+15	Ω	IEC 60093

Table 4 of 6

3 rows

Characteristic	Value	Method
Flammability Rate (0.8 mm thickness)	HB	UL94
Flammability Rate (1.6 mm thickness)	HB	UL94
Flammability Rate (3.2 mm thickness)	HB	UL94

Table 5 of 6

4 rows

Characteristic	Value	Unit	Method
Melt Temperature	210-255	°C	CYLINDER
Mould Temperature	45-70	°C	MOULD
Drying Temperature	80.0	°C	—
Dry Time	2.0	h	—

Table 6 of 6