To catalogue
Formac Black Formamid 6.6
- Chemical Family
- Polyamides
Formac Black Formamid 6.6 is used for automotive & farming mechanics, consumer goods and industrial applications. It has good mechanical strength, stiffness, heat resistance and wear resistance. It is a medium viscosity, for injection molding grade.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Lawn & Garden; Consumer Goods — Other Consumer Goods Applications; Consumer Goods — Sports & Recreation
Automotive & Transportation — Automotive
- Interior
- Other Automotive Applications
- Powertrain & UTH
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Formamid
- Polymer Name
- Polyamide 66 (PA 66)
- Flexural Modulus
- 2800.0 - 2800.0 MPa
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Automotive & Transportation
- Consumer Goods
- Industrial
- Technology
- Plastics
- Material Features
- Excellent Mechanical Strength
- Good Stiffness
- Heat Resistance
- Medium Viscosity
- Wear Resistant
- Certifications and Compliance
- ISO 9001
- UL 94
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Automotive Under The Hood
- Consumer Applications
- Doors
- Industrial Parts
- Sporting Goods
- Windows
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Point (DSC) | 260.0 | °C | ISO 3146 |
Table 2 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 3000.0 | MPa | ISO 527 - 2 |
| Tensile Stress Yield | 82.0 | MPa | ISO 527 - 2 |
| Strain at Break | 5.0 | % | ISO 527 - 2 |
| Flexural Modulus | 2800.0 | MPa | ISO 178 |
| Maximum Flexural Stress | 90.0 | MPa | ISO 178 |
| IZOD Notched Impact Strength (+23°C) | 4 - 5 | KJ/m2 | ISO 180/1eA |
Table 3 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Distortion Temperature (Under 1.8 Mpa Load, HDT A) | 73.0 | °C | ISO 75 - 2 |
| Heat Distortion Temperature (Under 0.45 MPa Load, HDT B) | 217.0 | °C | ISO 75 - 2 |
| Vicat Softening Point (Under 0.49 N Load, Vicat B) | 248.0 | °C | ISO 306 |
Table 4 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | 10000000000000.0 | Ω*cm | IEC 60093 |
| Surface Resistivity | 100000000000000.0 | Ω | IEC 60093 |
| Comparative Tracking Index | 500.0 | V | IEC 60112 |
Table 5 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Temperature | 270 - 290 | °C | CYLINDER |
| Melt Mold | 80.0 | °C | MOLD |
| Drying Temperature | 80.0 | °C | — |
| Dry Time | 3 - 6 | h | — |
Table 6 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.14 | g/cm3 | ISO 1183 |
| Humidity Absorption | 2.8 | % | Similar ISO 62 |
| Water Absorption (23°C 50% r.U) | 5.0 | % | ISO 62 |
| Melt Volume-Flow Rate (275°C 5kg) | 110.0 | °C | ISO 1133 |
| Molding Shrinkage (Parallel) | 1.0 - 1.15 | % | ISO 294-4 |
| Molding Shrinkage (Normal) | 1.15 - 1.4 | % | ISO 294-4 |