Tasnee PP H3030

Chemical Family: PolyolefinsPolypropylenes (PP)

Tasnee PP H3030 is a Polypropylene Homopolymer with a Melt Flow Rate (MFR) of 3.0 g/10min. Tasnee PP H3030 is designed for Bi-axial Oriented Polypropylene (BOPP) film applications, offering excellent transparency and gloss, high stiffness and excellent processability. Tasnee PP H3030 is formulated to be used for both general purpose and metallized films.

Properties

Physical Form: Pellets
Solid

Product families

Applications

Printing & Packaging — Packaging

Food & Beverage Packaging
Industrial & Transport Packaging
Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Adhesives & Sealants — Packaging & Paper

Tape & Label Adhesives

Printing & Packaging — Tapes, Labels & Adhesives

Tapes & Labels

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Brand: Tasnee PP
Polymer Name: Polypropylene Homopolymer (HPP)
Melt Flow Index: 3.0 - 3.0 g/10 min
Processing Methods: Extrusion
Color: Translucent
White
Markets: Adhesives & Sealants
Personal Care
Printing & Packaging
Technology: Plastics
Packaging Type: Bags
Labeling Claims: Food Contact Acceptable
Material Features: Excellent Transparency Properties
Food Contact Acceptable
Good Processability
High Gloss
High Stiffness
Typical Processing Conditions: Note: Processing parameters should only be used as guidelines. The above properties values are not to be construed as specifications.
Plastics and Elastomers End Uses: Biaxially Oriented Film
Film
Flexible Packaging
Food Packaging
General Purpose
Heavy Duty Bags
Labels
Oriented Film
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Extrusion

Technical data

Table 1 of 2

5 rows

Characteristic	Value	Unit	Method
Charpy Notched Impact Strength (at 23°C)	4	kJ/m2	ISO 179/1eA
Flexural Modulus (1% Secant)	1450	MPa	ISO 178
Rockwell Hardness	100	R	ISO 2039-2
Tensile Elongation at Yield	10	%	ISO 527-2
Tensile Strength at Yield	33	MPa	ISO 527-2