TALENE M4012 GY01

Chemical Family: PolyolefinsPolypropylenes (PP)

TALENE M4012 GY01 is a 40% talc filled polypropylene homopolymer with good flow and high stiffness. It has high long term heat aging stability. The product is available in gray color (RAL 7037). It is not intended for medical, pharmaceutical and/or drinking water applications.

Properties

Physical Form: Pellets
Solid

Product families

Applications

Automotive & Transportation — Automotive

Automotive Lighting

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Brand: TALENE
Polymer Name: Polypropylene Homopolymer (HPP)
Melt Flow Index: 12.0 - 12.0 g/10 min
Fillers Included: Talc
Processing Methods: Extrusion
Color: Grey
Markets: Automotive & Transportation
Technology: Plastics
Packaging Type: Bags
Material Features: Good Flow
Good Stiffness
Heat Aging Resistant
Odorless
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Extrusion

Technical data

Table 1 of 2

8 rows

Characteristic	Value	Unit	Method
Charpy Notched Impact Strength (at 23°C, Type1, Edgewise, Notch A)	2.2	kJ/m2	ISO 179
Charpy Unnotched Impact Strength (at 23°C, Type1, Edgewise)	26	kJ/m2	ISO 179
Flexural Modulus	3700	MPa	ISO 178
Flexural Strength (3.5%)	47	MPa	ISO 178
Tensile Modulus (Secant)	3200	MPa	ISO 527-1,-2
Tensile Strain at Break (50 mm/min)	7	%	ISO 527-1,-2
Tensile Strain at Yield (50 mm/min)	4	%	ISO 527-1,-2
Tensile Stress at Yield (at 50 mm/min)	30	MPa	ISO 527-1,-2

Table 2 of 2

5 rows

Characteristic	Value	Unit	Method
Density	1.22	g/cm3	ISO 1183
Heat Distortion Temperature (at 0.45 MPa)	119	°C	ISO 75B-1, -2
Heat Distortion Temperature (at 1.80 MPa)	70	°C	ISO 75A-1, -2
Melt Flow Rate (230°C / 2.16 kg)	12	g / 10 min	ISO 1133
Vicat Softening Temperature (B50, 50°C/h,50N)	89	°C	ISO 306