Tasnee HDPE 100 Orange
- Chemical Family
- PolyethylenesPolyolefins
Tasnee HD 100 Orange is a High Density Polyethylene, orange colored resin. The product is classified as PE 100. Tasnee HD 100 Orange provides excellent environmental stress cracking resistance properties (ESCR) with very good long term hydrostatic strength and combines very high impact and stiffness properties.
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Industrial — Oil, Gas & Mining
- Midstream
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Tasnee HDPE
- Polymer Name
- High Density Polyethylene (HDPE)
- Melt Flow Index
- 0.23 - 0.23 g/10 min, 6.4 - 6.4 g/10 min
- Processing Methods
- Injection Molding
- Color
- Orange
- Markets
- Industrial
- Technology
- Plastics
- Packaging Type
- Bags
- Material Features
Good Environmental Stress Crack Resistance (ESCR); Good Stiffness; High Impact Performance; Hydrostatic Strength; Odorless
- Plastics and Elastomers End Uses
- Natural Gas Distribution
- Pipes
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 2
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Notched Impact Strength (at -30°C) | 15 | kJ/m2 | ISO 179 |
| Charpy Notched Impact Strength (at 23°C) | 29 | kJ/m2 | ISO 179 |
| Flexural Creep Modulus(4 Point loading method, 1 min-value) | 1100 | MPa | DIN 19537-2 |
| Flexural Creep Modulus(4 Point loading method, 2000 h-value) | 330 | MPa | DIN 19537-2 |
| Flexural Creep Modulus(4 Point loading method, 24 h-value) | 560 | MPa | DIN 19537-2 |
| Flexural Stress (at 3,5% deflection) | 20 | MPa | ISO 178 |
| FNCT (4.0 MPa, 2% Arkopal N 100, 80°C) | min.1000 | h | ISO 16770 |
| Injection Molding Melt Temperature | 200 - 280 | °C | — |
| Maximum Elongation TD | min.350 | % | EN 638 |
| Melt Temperature | 190 - 220 | °C | — |
| MRS Classification | 10 | MPa | ISO/TR 9080 |
| Oxidation Induction Time (OIT, 210°C) | min. 30 | minute | EN 728 |
Table 2 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 0.951 | g/cm3 | ISO 1183 |
| Melt Flow Rate (190°C / 21.6 kg) | 6.4 | g/10 min | ISO 1133 |
| Melt Flow Rate (190°C / 5kg) | 0.23 | g / 10 min | ISO 1133 |
| Staudinger Index Jg | 380 | ml/g | ISO 1628 |
| Vicat Softening Temperature (VST/B/50 K/h (50N)) | 74 | °C | ISO 306 |