Tasnee PP H1030

Chemical Family: PolyolefinsPolypropylenes (PP)

Tasnee PP H1030 is a Polypropylene Homopolymer with a Melt Flow Rate (MFR) of 3 g/10min. Tasnee PP H1030 is designed for stretch tape from water bath and chill roll, offering low water-carry-over and low shrinkage. Its good mechanical properties and compliance to food contact regulations allow it to be used in various applications.

Properties

Physical Form: Pellets
Solid

Product families

Applications

Building & Construction — Building Materials
Consumer Goods — Carpet & Upholstery

Building & Construction — Building Envelope & Roofing

Waterproofing & Weatherproofing

Building & Construction — Decorative Materials & Finishes

Carpet

Industrial — Leather & Textiles

Technical Fabrics

Printing & Packaging — Packaging

Industrial & Transport Packaging

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Brand

Tasnee PP

Polymer Name

Polypropylene Homopolymer (HPP)

Melt Flow Index

3.0 - 3.0 g/10 min

Processing Methods

Extrusion, Injection Molding

Color

Translucent
White

Markets

Building & Construction
Consumer Goods
Industrial
Printing & Packaging

Technology

Plastics

Packaging Type

Bags

Labeling Claims

Food Contact Acceptable

Material Features

Food Contact Acceptable
Good Mechanical Properties
Low Shrinkage
Low Water Carryover
Odorless

Plastics and Elastomers End Uses

Carpet Backing
Cement Bags
Geo Membranes
Geotextiles
Heavy Duty Bags
Rope
Shrink Wrap
Tape

Plastics and Elastomers Functions

Resin

Typical Processing Conditions for Tapes

Extrusion Temperatures: 220 ~ 265 °C Water Bath Temperature : 35 ~ 45 °C
: Orientation Temperatures
Draw Ratio: 1:5 to 1:7
Note: Processing parameters should only be used as guidelines. The above properties values are not to be construed as specifications.

Plastics and Elastomers Processing Methods

Extrusion
Injection Molding

Technical data

Table 1 of 2

5 rows

Characteristic	Value	Unit	Method
Charpy Notched Impact Strength (at 23°C)	4	kJ/m2	ISO 179/1eA
Flexural Modulus (1% Secant)	1450	MPa	ISO 178
Rockwell Hardness	100	R	ISO 2039-2
Tensile Elongation at Yield	10	%	ISO 527-2
Tensile Strength at Yield	33	MPa	ISO 527-2