Tasnee LDPE 0725N
- Chemical Family
- PolyethylenesPolyolefins
Tasnee LD 0725N is a Low Density Polyethylene with a Melt Flow Rate of 0.75 g/10min (190°C/2.16kg), recommended for mono and multilayer blown film extrusion. Tasnee LD 0725N is an additive free grade and has a suitable molecular structure to make film with excellent mechanical and optical properties. Tasnee LD 0725N can be easily processed on all types of extruders designed for polyethylene. The melt temperature is suggested to be in the range of 170 – 220°C. Excellent properties of the film are achieved with a blow-up ratio of 2:1 and recommended film thickness range from 25 to 100 μm.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Printing & Packaging — Packaging
- Food & Beverage Packaging
- Industrial & Transport Packaging
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Tasnee LDPE
- Polymer Name
- Low Density Polyethylene (LDPE)
- Melt Flow Index
- 0.75 - 0.75 g/10 min
- Processing Methods
- Blown Film Extrusion, Extrusion, Film Extrusion
- Color
- Translucent
- White
- Markets
- Printing & Packaging
- Technology
- Plastics
- Packaging Type
- Bags
- Labeling Claims
- Additive-free
- Food Contact Acceptable
- Material Features
- Food Contact Acceptable
- Good Mechanical Properties
- Good Optical Properties
- Odorless
- Plastics and Elastomers End Uses
- Film
- Food Packaging
- Form Fill Seal Packaging
- Retort Pouches
- Shrink Wrap
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blown Film Extrusion
- Extrusion
- Film Extrusion
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 0.923 | g/cm3 | ISO 1183 |
| Melt Flow Rate (190°C / 2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Melting Temperature | 111 | °C | ISO 3146 |
| Vicat Softening Temperature (A50 (500C/h 10N)) | 96 | °C | ISO 306 |
Table 2 of 3
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 260 | MPa | ISO 527-1,-2 |
| Tensile Stress at Yield | 11 | MPa | ISO 527-1,-2 |
| Tensile Strain at Break (MD / TD) | 300 / 600 | % | ISO 527-1,-3 |
| Coefficient of Friction | min. 80 | % | ISO 8295 |
| Dart Drop Impact (50 μm) | 150 | g | ASTM D 1709 |
| Tensile Strength (MD / TD) | 26 / 24 | % | ISO 527-1,-3 |
Table 3 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Gloss (at 20°) | min. 40 | GU | ASTM D 2457 |
| Gloss (at 60°) | min. 90 | GU | ASTM D 2457 |
| Haze | max. 8 | % | ASTM D 1003 |