Tasnee PP H5020K

Chemical Family: PolyolefinsPolypropylenes (PP)

Tasnee PP H5020K is a Polypropylene Homopolymer with a Melt Flow Rate (MFR) of 3.0 g/10min. Tasnee PP H5020K is designed for caps and closures. It is particularly formulated to meet the opening torque requirements for screw caps and closures. It combines outstanding balance of high stiffness and improved isotropic dimension stability with good processability and has anti-static protection.

Properties

Physical Form: Pellets
Solid

Product families

Applications

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Brand: Tasnee PP
Polymer Name: Polypropylene Homopolymer (HPP)
Melt Flow Index: 3.0 - 3.0 g/10 min
Processing Methods: Compression Molding, Extrusion
Color: Translucent
White
Markets: Printing & Packaging
Technology: Plastics
Packaging Type: Bags
Material Features: Anti-Static
Dimensional Stability
Good Processability
Good Stiffness
Typical Processing Conditions: Note: Processing parameters should only be used as guidelines. The above properties values are not to be construed as specifications.
Plastics and Elastomers End Uses: Caps
Closures
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Compression Molding
Extrusion

Technical data

Table 1 of 2

7 rows

Characteristic	Value	Unit	Method
Flexural Modulus (1% Secant)	1500	MPa	ISO 178
Izod Notched Impact Strength (at 23 °C)	3.5	kJ/m2	ISO 180-1A
Rockwell Hardness	100	R	ISO 2039-2
Tensile Elongation at Break	min. 50	%	ISO 527-2
Tensile Elongation at Yield	8.4	%	ISO 527-2
Tensile Modulus	1800	MPa	ISO 527-2
Tensile Strength at Yield	35	MPa	ISO 527-2

Table 2 of 2

5 rows

Characteristic	Value	Unit	Method
Density	0.9	g/cm3	ISO 1183
Heat Distortion Temperature (at 0.45 MPa)	100	°C	ISO 75-2
Melt Flow Rate (230°C / 2.16 kg)	3	g / 10 min	ISO 1133
Melting Temperature	165	°C	ISO 11357-3
Vicat Softening Temperature	152	°C	ISO 306