Tasnee PP H1045

Chemical Family: PolyolefinsPolypropylenes (PP)

Tasnee PP H1045 is a Polypropylene Homopolymer with a Melt Flow Rate (MFR) of 4.5 g/10min. Tasnee PP H1045 is designed for high extrusion speed lines to make stretch tapes, offering low water-carry-over and low shrinkage. Good balance of strength, shrinkage, splitting tendency. It is compliant to food contact regulations.

Properties

Physical Form: Granules
Solid

Product families

Applications

Building & Construction — Building Materials
Consumer Goods — Carpet & Upholstery
Consumer Goods — Sports & Recreation

Building & Construction — Building Envelope & Roofing

Waterproofing & Weatherproofing

Building & Construction — Decorative Materials & Finishes

Carpet

Industrial — Leather & Textiles

Technical Fabrics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Brand

Tasnee PP

Polymer Name

Polypropylene Homopolymer (HPP)

Melt Flow Index

4.5 - 4.5 g/10 min

Processing Methods

Extrusion

Color

Translucent
White

Markets

Building & Construction
Consumer Goods
Industrial

Technology

Plastics

Packaging Type

Bags

Labeling Claims

Food Contact Acceptable

Material Features

Excellent Balance of Strength
Food Contact Acceptable
High Extrusion Speed
Low Shrinkage
Low Water Carryover

Typical Processing Conditions

Extrusion Temperatures: 200 ~ 260 °C c
: Orientation Temperatures
Draw Ratio: 1:6 to 1:8
Note: Processing parameters should only be used as guidelines. The above properties values are not to be construed as specifications.

Plastics and Elastomers End Uses

Carpet Backing
Fabrics
Geo Membranes
Geotextiles
Industrial Applications
Sporting Goods
Tape

Plastics and Elastomers Functions

Resin

Plastics and Elastomers Processing Methods

Extrusion

Technical data

Table 1 of 2

5 rows

Characteristic	Value	Unit	Method
Charpy Notched Impact Strength (at 23°C)	3.5	kJ/m2	ISO 179/1eA
Flexural Modulus (1% Secant)	1500	MPa	ISO 178
Rockwell Hardness	100	R	ISO 2039-2
Tensile Elongation at Yield	9	%	ISO 527-2
Tensile Strength at Yield	34	MPa	ISO 527-2

Table 2 of 2