TALENE M4012 B01
- Chemical Family
- PolyolefinsPolypropylenes (PP)
TALENE M4012 B01 is a 40% talc filled polypropylene homopolymer with good flow and high stiffness. It has high long term heat aging stability. It is designed for injection molding applications for interior automotive parts with good dimensional stability. The product is available in black color. It is not intended for medical, pharmaceutical and/or drinking water applications.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Automotive & Transportation — Automotive
- Fuel Systems
- Interior
- Powertrain & UTH
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- TALENE
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 12.0 - 12.0 g/10 min
- Fillers Included
- Talc
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Packaging Type
- Bags
- Material Features
- Dimensional Stability
- Good Flow
- Good Stiffness
- Heat Aging Resistant
- Odorless
- Plastics and Elastomers End Uses
- Automotive Fuel Structural Components
- Automotive Interior Parts
- Automotive Under The Hood
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Ball indentation hardness (H 358/30) | 78 | MPa | ISO 2039-1 |
| Charpy Notched Impact Strength (at 23°C, Type1, Edgewise, Notch A) | 3 | kJ/m2 | ISO 179 |
| Charpy Unnotched Impact Strength (at 23°C, Type1, Edgewise) | 26 | kJ/m2 | ISO 179 |
| Flexural Modulus | 4300 | MPa | ISO 178 |
| Flexural Strength (3.5%) | 49 | MPa | ISO 178 |
| Tensile Modulus (Secant) | 4000 | MPa | ISO 527-1,-2 |
| Tensile Strain at Break (50 mm/min) | 6 | % | ISO 527-1,-2 |
| Tensile Strain at Yield (50 mm/min) | 3 | % | ISO 527-1,-2 |
| Tensile Stress at Break (at 50 mm/min) | 32 | MPa | ISO 527-1,-2 |
| Tensile Stress at Yield (at 50 mm/min) | 35 | MPa | ISO 527-1,-2 |
Table 2 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.2 | g/cm3 | ISO 1183 |
| Heat Distortion Temperature (at 0.45 MPa) | 140 | °C | ISO 75B-1, -2 |
| Heat Distortion Temperature (at 1.80 MPa) | 68 | °C | ISO 75A-1, -2 |
| Melt Flow Rate (230°C / 2.16 kg) | 12 | g / 10 min | ISO 1133 |
| Vicat Softening Temperature (B50, 50°C/h,50N) | 93 | °C | ISO 306 |