Tasnee LDPE 4025N
- Chemical Family
- PolyethylenesPolyolefins
Tasnee LD 4025N is an Additive Free Low Density Polyethylene with Melt Flow Rate of 4.0 g/10min (190°C/2.16kg). It has a suitable molecular structure to produce film with excellent mechanical properties. Tasnee LD 4025N can be easily processed on all types of extruders designed for polyethylene. The melt temperature is suggested to be in the range of 150 – 190°C. Excellent properties of the film are achieved with a blow-up ratio of 2.5:1 and recommended film thickness range from 15 to 40 μm.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Printing & Packaging — Packaging
- Food & Beverage Packaging
- Industrial & Transport Packaging
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Tasnee LDPE
- Polymer Name
- Low Density Polyethylene (LDPE)
- Melt Flow Index
- 4.0 - 4.0 g/10 min
- Processing Methods
- Blown Film Extrusion, Extrusion, Film Extrusion
- Color
- Translucent
- White
- Markets
- Printing & Packaging
- Technology
- Plastics
- Packaging Type
- Bags
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Food Contact Acceptable
- Good Mechanical Properties
- Odorless
- Plastics and Elastomers End Uses
- Cast Films
- Film
- Food Packaging
- Form Fill Seal Packaging
- Retort Pouches
- Shrink Wrap
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blown Film Extrusion
- Extrusion
- Film Extrusion
Technical data
Table 1 of 3
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Break (MD / TD) | 22 / 17 | % | ISO 527-1,-3 |
| Tensile Modulus | 260 | MPa | ISO 527-1,-2 |
| Tensile Stress at Yield | 11 | MPa | ISO 527-1,-2 |
| Dart Drop Impact (50 μm) | 100 | g | ASTM D 1709 |
| Tensile Strain at Break (MD / TD) | 300 / 600 | % | ISO 527-1,-3 |
| Coefficient of Friction | min. 70 | % | ISO 8295 |
Table 2 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 0.924 | g/cm3 | ISO 1183 |
| Melt Flow Rate (190°C / 2.16 kg) | 4 | g/10 min | ISO 1133 |
| Melting Temperature | 111 | °C | ISO 3146 |
| Vicat Softening Temperature (A50 (50 OC/h 10N)) | 92 | °C | ISO 306 |
Table 3 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Gloss (at 20°) | min. 60 | GU | ASTM D 2457 |
| Gloss (at 60°) | min. 105 | GU | ASTM D 2457 |
| Haze | max. 8.0 | % | ASTM D 1003 |