Ebalta Kunststoff Gmbh MG 804MG 804 1
- Chemical Family
- Polyurethanes (PU)
This product is a polyurethane system. The processing is preferably made in customary vacuum pouring plant. Manual processing possible. Maximum wall thicknesses of the parts: from 5 – 10 mm.
Product families
Applications
- Tooling & Moldmaking
Product Families
- Polyurethanes
Other characteristics
- Density
- 1080.0 - 1120.0 kg/m³
- End Uses
- Modeling Material
- Polymer Name
- Polyurethane (unspecified)
- Tensile Strength
- 44.0 - 60.0 MPa
- Processing Methods
- Casting
- Basis
- Prototype casting resin MG 804-1
- Markets
- Industrial
- Storing
Storage at room temperature 18-25 °C. Opened containers should be closed immediately after use and should be used up as soon as possible.
- Properties
long potlife very well castable good impact strength easily dyeable low agressivenes against silicones RoHS conform
- Technology
- Plastics
- Material Features
- Good Impact Strength
- Processing Instruction
Stir up comp. A before use, since additives tend to sedimentation. Higher heat resistance is reached with MG 804-1. To get a better E-modulus, e.g. more stiffness of the parts glass fiber paste MG 804 GF could be used. With only this product the maximum stiffness can be achieved. Due to higher viscosity the casting has to be made in a vacuum chamber. Further data sheets:; MG 804 /MG 804-1;; MG 804 GF/MG 804-1;; MG 804 , MG 804 GF/MG 804-1; Processing parameters: Temperature of resin: 20-30°C / Temperature of mold: 60 - 70°C. In order to get bubble-free parts, we recommend working under vacuum. Straight before casting, we recommend a one-time air impact from 10 of 60-70 mbar. Mouldmaterial: we recommend silicone molds, for example Silastic® RTV 4234-T4
- Certifications and Compliance
- RoHS Compliant
- Compatible Polymers and Resins
- Acrylonitrile Butadiene Styrene (ABS)
- Polyamides
- Plastics and Elastomers End Uses
- Modeling Material
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Casting
Technical data
Table 1 of 1
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| TG in TMA TG | 87 | °C | — |
| Density (20°C) | 1,10 ± 0,02 | g/cm3 | — |
| Elongation of tensile strength | 12 ± 2 | % | — |
| Pot Life (20°C) | 8-11 | minutes | — |
| Flexural elongation at break | 6.3 ± 0.2 | % | EN ISO 178 |
| Curing time at RT | 45 - 60 | Hrs | — |
| Flexural modulus | 1975 ± 150 | MPa | EN ISO 178 |
| Post Curing | 4-60 | Time in h (Temperature in °C) | — |
| Flexural strength | 80 ± 5 | MPa | EN ISO 178 |
| Flexural strength | 85 ± 5 | MPa | EN ISO 178 |
| Heat resistance (HDT) | 82 ± 3 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 31 ± 6 | kJ/m2 | EN ISO 179 |