Ebalta Kunststoff Gmbh GM 956GM 956 70
- Chemical Family
- Polyurethanes (PU)
This product is a polyurethane system. After use please close the containers carefully. The product can be subject to color variations due to raw materials, but these color variations have no influence on the quality and the properties of the product. Seal porous mold surfaces first (ebalta mold sealer). For optimum mold releasing we recommend a special release agent (like T1-1), which can be applied easily with a brush or be sprayed. Releasing of the mold 2-3 times, evaporate for about 20 min. after each releasing.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Cooling & Climate
- Fuel Systems
- Tires
- Other Industrial Applications
- Tubing & Fluids Handling
- Flexible Packaging Adhesives
- Flexible Packaging Adhesives
Product Families
- Polyurethanes
Other characteristics
- Density
- 1020.0 - 1060.0 kg/m³
- End Uses
- Tires, Tubing
- Polymer Name
- Polyurethane (unspecified)
- Tensile Strength
- 4.6 - 5.6 MPa
- Basis
- Flexible casting resin
- Markets
- Adhesives & Sealants
- Automotive & Transportation
- Consumer Goods
- Healthcare & Pharma
- Industrial
- Printing & Packaging
- Storing
Storage at room temperature 18-25 °C.; Opened containers should be closed immediately after use and should be used up as soon as possible.; Shelf life is indicated on the labels.
- Properties
shore A hardness 75 excellent flow properties odorless high tear strength free of mercury
- Technology
- Plastics
- Material Features
- Excellent Flow Properties
- Good Tear Strength
- Mercury Free
- Odorless
- Package Unit
Units; Comp. A GM 956 Comp. A (Isocyanate) 1,000 kg / 5,000 kg; Comp. B GM 956-70 Comp.B (Pol.) 1,100 kg
- Processing Instruction
Material- and processing temperature between 18°C and 25°C. Mixing ratio resin and hardener according instructions. Mold temperature for fabircation of vacuum casting parts: 70°C Final properties reached after 7 days at room temperature or 4 hrs. post curing at 70°C Any resin residues at mixing rods, can be removed with ebalta cleaning Agent. To accelerate use our Accelerator 08.
- Plastics and Elastomers End Uses
- Tires
- Tubing
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 1
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile strength | 5.1 ± 0.5 | MPa | ISO 37 |
| Viscosity (25°C) | 2000 ± 200 | mPa.s | — |
| Elongation at break / test piece type 2 | 700 ± 100 | % | ISO 37 |
| Density (20°C) | 1,04 ± 0,02 | g/cm3 | — |
| Shore hardness | 70 ± 3 | Shore A | DIN ISO 7619-1 |
| Pot Life (200g/20°C) | 15 - 20 | minutes | — |
| Tear resistance arch shaped test piece with incision 1 mm | 12 ± 1 | kN/m | DIN ISO 34-1 |
| Curing Time (70°C) | 2 | Hrs | — |