Ebalta Kunststoff Gmbh GM 956 90Comp. A+B
- Chemical Family
- Polyurethanes (PU)
This product is a polyurethane system. "VP"-products are experimental products. Regarding technical data slight modifications are possible.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Cooling & Climate
- Fuel Systems
- Interior
- Tires
- Other Industrial Applications
- Consumer Electronics
- Tubing & Fluids Handling
Product Families
- Polyurethanes
Other characteristics
- Density
- 1030.0 - 1070.0 kg/m³
- End Uses
- Flexible Grips, Tires, Tubing
- Polymer Name
- Polyurethane (unspecified)
- Tensile Strength
- 6.0 - 8.0 MPa
- Basis
- Flexible casting resin
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Storing
Storage at room temperature 18-25 °C. Opened containers should be closed immediately after use and should be used up as soon as possible. Shelf life is indicated on the labels.
- Properties
shore A hardness 90 excellent flow properties transparent easily dyeable odorless high tear strength free of mercury RoHS conform
- Technology
- Plastics
- Quality Standards
- DIN
- Material Features
- Excellent Flow Properties
- Good Tear Strength
- Mercury Free
- Odorless
- Package Unit
Units; Comp. A GM 956-90 Comp. A (Isocyanate) 4,000 kg; Comp. B GM 956-90 Comp. B (Pol) 5,000 kg / 25,000 kg
- Processing Instruction
Material- and processing temperature: between 18 - 25 °C. Close containers after use. Seal porous mold surfaces first (ebalta mold sealer). For optimum mold releasing we recommend a special release agent (like T1-1), which can be applied easily with a brush or be sprayed. Releasing of the mold 2-3 times, evaporate for about 20 min. after each releasing. Mixing ratio resin/hardener according to instructions. Both components can be easily mixed free from air bubbles in small quantities by hand with a round stirring rod or in larger quantities with a spiral stirrer. The processing in a vacuum is also possible. Stirring rods etc. with residual resin can be easily cleaned with ebaclean.
- Certifications and Compliance
- RoHS Compliant
- Plastics and Elastomers End Uses
- Flexible Grips
- Tires
- Tubing
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 1
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Viscosity (25°C) | 2000 ± 200 | mPa.s | — |
| Elongation at break / test piece type 2 | 280 ± 30 | % | ISO 37 |
| Elongation at break / test piece type 2 | 600 ± 60 | % | ISO 37 |
| Density (20°C) | 1,05 ± 0,02 | g/cm3 | — |
| Gel Time (200g/20°C) | 18 - 22 | minutes | — |
| Shore hardness | 90 ± 3 | Shore D | DIN ISO 7619-1 |
| Shore hardness | 43 ± 3 | Shore A | DIN ISO 7619-1 |
| Curing time at RT | 6-10 | Hrs | — |
| Curing Time (70°C) | 1-2 | Hrs | — |
| Tear resistance arch shaped test piece with incision 1 mm | 48 ± 3 | kN/m | DIN ISO 34-1 |
| Tear resistance arch shaped test piece with incision 1 mm | 5.0 ± 0.5 | kN/m | DIN ISO 34-1 |
| Tensile strength | 3 ± 0.5 | MPa | ISO 37 |