Ebalta Kunststoff Gmbh SG 131PUR 11
- Chemical Family
- Polyurethanes (PU)
Ebalta SG 131 / PUR 11 is a Polyurethane system. Material should be carefully stirred up/ shaked before use. Filler content and sales units are on the separate mixing table noted.
Product families
Applications
- Interior Fixtures
- Equipment & Parts
- Tooling & Moldmaking
Product Families
- Polyurethanes
Other characteristics
- Density
- 1040.0 - 1080.0 kg/m³
- End Uses
Foundry Dressings, Modeling Material, Molds/Dies/Tools, Power/Other Tools, Tooling
- Polymer Name
- Polyurethane (unspecified)
- Processing Methods
- Casting
- Markets
- Building & Construction
- Industrial
- Storing
Storage at room temperature 18-25 °C.; Opened containers should be closed immediately after use and should be used up as soon as possible.
- Packages
- 1,000 kg / 5,000 kg / 50,000 kg
- Technology
- Plastics
- Material Features
- High Strength
- Processing Instruction
The fillers should be stirred into the single components A and B, so that they have nearly the same viscosity.. After that both components can be very well mixed. In case of small quantities and sufficient experience it is also possible to mix the unfilled components first and then to stir in the filler, without making the potlife too short for casting.
- Plastics and Elastomers End Uses
- Foundry Dressings
- Modeling Material
- Molds/Dies/Tools
- Power/Other Tools
- Tooling
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Casting
Technical data
Table 1 of 1
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 67 ± 2 | Shore A | DIN ISO 7619-1 |
| Compressive Strength | 34 ± 3 | MPa | EN ISO 604 |
| Viscosity (25°C) | 200 ± 80 | mPa.s | — |
| Compressive Strength | 32 ± 5 | MPa | EN ISO 604 |
| Flexural elongation at break | 7.6 ± 0.3 | % | EN ISO 178 |
| Density (20°C) | 1,06 ± 0,02 | g/cm3 | — |
| Flexural modulus | 1000 ± 100 | MPa | EN ISO 178 |
| Pot Life (200g/20°C) | 9-15 | minutes | — |
| Impact resistance (Charpy) | 20 ± 4 | kJ/m2 | EN ISO 179 |
| Curing time at RT | 5-8 | Hrs | — |
| Flexural Strength | 38 ± 5 | MPa | EN ISO 178 |
| Flexural Elongation at Break | 7,6 ± 0,3 | % | EN ISO 178 |