Ebalta Kunststoff Gmbh GH 706GL
- Chemical Family
- Epoxy & Epoxy Derivatives
Ebalta GH 706/GL is a well castable two-components epoxy resin, which cures at room temperature and can be casted 40 - 50 mm thickness. The resin GH 706 contains very fine hard fillers and with hardener GL it has got a very hard, wear resistant surface with high compression strength and very fine structure. Physical data as per test specimen cured for 8 hrs. at 80°C ebalta GH 706 is the castable version of the very hard gelcoat OH 6-1.
Product families
Applications
- Tooling & Moldmaking
Product Families
- Epoxies
Other characteristics
- End Uses
- Foundry Dressings, Modeling Material
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 80.4 - 85.6 MPa
- Processing Methods
- Casting
- Basis
- hard casting resin
- Markets
- Industrial
- Storing
Storage at room temperature 18-25 °C. Opened containers should be closed immediately after use and should be used up as soon as possible.. Shelf life: see labels
- Properties
abrasion resistant fine structure good compressive strength very hard wear resistant well castable castable up to 30 mm
- Technology
- Plastics
- Material Features
- Good Abrasion Resistance
- Good Compressive Strength
- High Hardness
- Wear Resistant
- Package Unit
Packing size A-Pack GH 706 / GL resin 6 x 1,250 kg / hardener 6 x 0,125 kg = 8,250 kg; Units; Resin GH 706 8,000 kg Hardener GL 1,5000 kg / 5,000 kg
- Processing Instruction
The temperature of material and processing should be between 18 and 25° C. Filled systems should be stirred thoroughly before use. After each use the containers have to be closed again. Porous mold surfaces should be sealed before ( ebalta sealant ). For an optimum mold release we recommend a suitable release agent (e.g. T 1-1) which can be easily applied with a brush. The mold should be treated 2 or 3 times with release agent and allowed to evaporate for approx. 20 min after every application. Mixing ratio resin/hardener according to instructions! To get a clean component part , we recommend upward flow casting and to take care of sufficient venting. Resin residues at stirring rods and so on can be easily cleaned with our ebaclean.
- Plastics and Elastomers End Uses
- Foundry Dressings
- Modeling Material
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Casting
Technical data
Table 1 of 1
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Wear jet test | 357 | W(V/t) [mm³/min] | — |
| Viscosity (25°C) | 10000 ± 2000 | mPa.s | — |
| Coefficient of linear expansion 20 - 50 °C | 60 | 10-6K-1 | — |
| Density (20°C) | 2,05 ± 0,05 | g/cm3 | — |
| Compressive Strength | 104 ± 4 | MPa | EN ISO 604 |
| Pot Life (200g/20°C) | 30 - 40 | minutes | — |
| Flexural elongation at break | 1.3 ± 0.07 | % | EN ISO 178 |
| Curing time at RT | 12-15 | Hrs | — |
| Flexural modulus | 8424 ± 380 | MPa | EN ISO 178 |
| Flexural strength | 83 ± 2.6 | MPa | EN ISO 178 |
| Heat resistance (HDT) | 67 ± 2 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 7 ± 1 | kJ/m2 | EN ISO 179 |