Ebalta Kunststoff Gmbh IH 16hardener fast
- Chemical Family
- Epoxy & Epoxy Derivatives
Ebalta IH 16 / hardener fast is a very thin liquid two component epoxy resin with high strength values and high mold resistance. Due to its good soaking and wet-out characteristics the resin/hardener mixture is suitable as infilitration resin for porouse printed parts.
Product families
- Epoxies
Other characteristics
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 125.0 - 145.0 MPa
- Processing Methods
- 3D Printing
- Basis
- Infiltration resin for porous parts
- Storing
At appropriate storage 18-25°C. Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours. Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible. Shelf life is indicated on the labels
- Applications
Flexural strength Flexural modulus Flexural elongation at break Impact resistance (Charpy) compressive strength 0,75 % proof stress Heat resistance (HDT) Shore hardness
- Availability
- At bigger quantities of >500g the working time will be clearly shorter.
- For ebalta IH 16 are 3 different hardeners available.
- IH 16 hardener slow
- pot life 300 - 400 min.
- IH 16 hardener fast
- pot life 50 - 60 min.
- IH 16 hardener very fast
- pot life 15 - 25 min. (for machine application)
- Technology
- Plastics
- Material Features
- High Strength
- Low Viscosity
- Package Unit
- 0,150 kg / 1,200 kg
- Processing Instruction
The temperature of material and processing should be between 18 and 25° C. The mixing of resin and hardener should be made intensively and if possible without any bubbles at room temperature.
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- 3D Printing
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 85 ± 3 | Shore D | DIN ISO 7619-1 |
| Viscosity (25°C) | 350 ± 50 | mPa.s | — |
| Compressive Strength 0,75 % proof stress | 105 ± 10 | MPa | — |
| Density (20°C) | 1,12 ± 0,02 | g/cm3 | — |
| Flexural elongation at break | 5.8 ± 0.1 | % | EN ISO 178 |
| Pot Life (200g/20°C) | 50 - 60 | minutes | — |
| Flexural modulus | 3520 ± 250 | MPa | EN ISO 178 |
| Curing time at RT | 20 - 30 | Hrs | — |
| Flexural strength | 135 ± 10 | MPa | EN ISO 178 |
| Heat resistance (HDT) | 78 ± 3 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 47 ± 11 | kJ/m2 | EN ISO 179 |