Ebalta Kunststoff Gmbh SG 700 APUR 5
- Chemical Family
- Polyurethanes (PU)
Ebalta SG 700 A / PUR 5 is a two-component-Polyurethane casting resin, which cures very fast at room temperature. The very good workability and the excellent mechanical properties makes SG 700 a material with versatile application possibilities. ebalta SG 700 A is even more abrasion-resistant, but not so well workable by machine. Displacements, even made of wood, can be filled in. Material should be carefully stirred up/ shaked before use.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Other Industrial Applications
- Tooling & Moldmaking
Product Families
Plastics — Thermoset Resins
- Polyurethanes
Other characteristics
- Density
- 1700.0 - 1800.0 kg/m³
- End Uses
Foundry Dressings, Industrial Castings, Modeling Material
- Polymer Name
- Polyurethane (unspecified)
- Processing Methods
- Casting
- Markets
- Industrial
- Packages
- 1,000 kg / 6,000 kg
- Properties
abrasion resistant well castable fine structure dimensionally accurate fast curing multi purpose useable
- Technology
- Plastics
- Material Features
- Abrasion Resistant
- Excellent Dimensional Accuracy
- Fast Curing
- Processing Instruction
Storage at room temperature 18-25 °C.; Opened containers should be closed immediately after use and should be used up as soon as possible.
- Plastics and Elastomers End Uses
- Foundry Dressings
- Industrial Castings
- Modeling Material
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Casting
Technical data
Table 1 of 1
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 83 ± 3 | Shore D | DIN ISO 7619-1 |
| Compressive Strength | 53 ± 5 | MPa | EN ISO 604 |
| Viscosity (25°C) | 1700 ± 350 | mPa.s | — |
| Flexural elongation at break | 1.4 ± 0.15 | % | EN ISO 178 |
| Density (20°C) | 1,75 ± 0,05 | g/cm3 | — |
| Flexural modulus | 4470 ± 450 | MPa | EN ISO 178 |
| Pot Life (200g/20°C) | 5-7 | minutes | — |
| Flexural strength | 43 ± 5 | MPa | EN ISO 178 |
| Curing time at RT | 1-2 | Hrs | — |
| Impact resistance (Charpy) | 4.7 ± 1 | kJ/m2 | EN ISO 179 |
| Flexural Strength | 43 ± 5 | MPa | EN ISO 178 |
| Flexural Elongation at Break | 1,4 ± 0,15 | % | EN ISO 178 |