Ebalta Kunststoff Gmbh GH 760GL
- Chemical Family
- Epoxy & Epoxy Derivatives
Ebalta GH 760/GL is a two-components epoxy resin, curing at room temperature, castable to 40 mm in open casting. The fine non-grinding fillers lead to good surface slip properties and mechanical workability. For this reason ebalta GH 760/GL is especially suitable for metal sheet tools as well as for foundry equipment. Due to its high strength and excellent dimensional accuracy this system is quite versatile.
Product families
Applications
- Equipment & Parts
- Tooling & Moldmaking
Product Families
- Epoxies
Other characteristics
- End Uses
Foundry Dressings, Molds/Dies/Tools, Power/Other Tools
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 90.0 - 110.0 MPa
- Processing Methods
- Casting
- Basis
- Casting resin with surface slip characteristics
- Markets
- Industrial
- Storing
Storage at room temperature (18-25 °C) in closed original container 9 months. Already opened containers should be closed immediately after use and should be used as soon as possible.
- Properties
dimensionally accurate abrasion resistant high strength castable until 40 mm very good sliding properties
- Technology
- Plastics
- Material Features
- Abrasion Resistant
- Excellent Dimensional Accuracy
- Good Sliding Properties
- High Strength
- Package Unit
Packing size B-Pack GH 760 / GL Resin 6 x 1,500 kg / Hardener 6 x 0,150 kg = 9,900 kg; Units; Resin GH 760 8,000 kg / 25,000 kg Hardener GL 1,5000 kg / 5,000 kg
- Processing Instruction
The temperature of material and processing should be between 18 and 25° C. Filled systems should be stirred thoroughly before use. After each use the containers have to be closed again. Porous mold surfaces should be sealed before ( ebalta sealant ). For an optimum mold release we recommend a suitable release agent (e.g. T 1-1) which can be easily applied with a brush. The mold should be treated 2 or 3 times with release agent and allowed to evaporate for approx. 20 min after every application. Mixing ratio resin/hardener according to instructions! To get a clean component part , we recommend upward flow casting and to take care of sufficient venting. Resin residues at stirring rods and so on can be easily cleaned with our ebaclean.
- Plastics and Elastomers End Uses
- Foundry Dressings
- Molds/Dies/Tools
- Power/Other Tools
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Casting
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Wear jet test | 257 | W(V/t) [mm³/min] | — |
| Viscosity (25°C) | 9500 ± 1000 | mPa.s | — |
| Coefficient of linear expansion 20 - 50 °C | 59 | 10-6K-1 | — |
| Density (20°C) | 2,20 ± 0,05 | g/cm3 | — |
| Compressive Strength | 120 ± 10 | MPa | EN ISO 604 |
| Pot Life (200g/20°C) | 45 - 55 | minutes | — |
| Flexural elongation at break | 1.50 ± 0.2 | % | EN ISO 178 |
| Curing time at RT | 18 - 24 | Hrs | — |
| Flexural modulus | 7250 ± 500 | MPa | EN ISO 178 |
| Flexural strength | 100 ± 10 | MPa | EN ISO 178 |
| Heat resistance (HDT) | 63 ± 2 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 9 ± 1.5 | kJ/m2 | EN ISO 179 |