Ebalta Kunststoff Gmbh AH 140LI 20
- Chemical Family
- Epoxy & Epoxy Derivatives
Ebalta AH 140 / LI 20 is a general purpose resin.
Product families
Applications
- Consumer Goods — Other Consumer Goods Applications
- Exterior & Body
- Interior
- Other Automotive Applications
Product Families
- Epoxies
Other characteristics
- End Uses
Automotive Applications, Automotive Exterior Parts, Automotive Interior Parts, General Purpose
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 113.0 - 133.0 MPa
- Markets
- Automotive & Transportation
- Consumer Goods
- Storing
At appropriate storage 18-25°C.; Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours.; Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible.
- Properties
- cures tack free
- Cure
- Chemical Cure
- Technology
- Plastics
- Material Features
- General Purpose
- Processing Instruction
The temperature of material and processing should be between 18 and 25° C.; The mixing of resin and hardener should be made intensively and if possible without any bubbles at room temperature.; We recommend a post curing with a temperature rise of about 10°C/hour. Difficult geometries should be supported during the curing cycle. Afterwards the part should be cooled down at about 20°C/hour.
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- General Purpose
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 1
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 87 ± 3 | Shore D | DIN ISO 7619-1 |
| Viscosity (25°C) | 600 ± 75 | mPa.s | — |
| Compressive Strength 0,75 % proof stress | 91 ± 5 | MPa | — |
| Density (20°C) | 1,12 ± 0,03 | g/cm3 | — |
| Flexural elongation at break | 6.7 ± 0.2 | % | EN ISO 178 |
| Pot Life (200g/20°C) | 18 - 22 | minutes | — |
| Flexural modulus | 3320 ± 250 | MPa | EN ISO 178 |
| Curing time at RT | 16 - 24 | Hrs | — |
| Flexural strength | 123 ± 10 | MPa | EN ISO 178 |
| Post Curing | 4 ( 120) | Time in h (Temperature in °C) | — |
| Glass transition temperature TG | 83 | °C | — |
| Heat resistance (HDT) | 91 ± 3 | °C | DIN EN ISO 75 B |