Ebalta Kunststoff Gmbh SG 130PUR 11
- Chemical Family
- Polyurethanes (PU)
This is a Polyurethane system. Material should be carefully stirred up/ shaked before use. Filler content and sales units are on the separate mixing table noted.
Product families
Applications
- Equipment & Parts
- Tooling & Moldmaking
Product Families
- Polyurethanes
Other characteristics
- Density
- 1080.0 - 1120.0 kg/m³
- End Uses
Foundry Dressings, Modeling Material, Molds/Dies/Tools, Power/Other Tools, Tooling
- Polymer Name
- Polyurethane (unspecified)
- Processing Methods
- Casting
- Basis
- High quality fast casting resin system
- Markets
- Industrial
- Storing
Storage at room temperature 18-25 °C. Opened containers should be closed immediately after use and should be used up as soon as possible. Shelf life is indicated on the labels.
- Properties
- unfilled impact resistant high strength
- Technology
- Plastics
- Material Features
- High Strength
- Impact Resistance
- Package Unit
Packing size A-Pack SG 130 / PUR 11 Resin 5 x 0,250 kg / Hardener 5 x 0,250 kg / Filler F-B 5 x 0,750 kg = 6,250 kg Units Resin SG 130 Comp. A 1,000 kg / 5,000 kg / 50,000 kg Hardener PUR 11 Comp. B 1,000 kg / 5,000 kg / 50,000 kg
- Processing Instruction
The fillers should be stirred into the single components A and B, so they have nearly the same viscosity. After the both components can be mixed very well. In case of small quantities and sufficient experience it is also possible to mix the unfilled components first and then to stir into the filler, without making the potlife too short for casting.
- Plastics and Elastomers End Uses
- Foundry Dressings
- Modeling Material
- Molds/Dies/Tools
- Power/Other Tools
- Tooling
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Casting
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 72 ± 2 | Shore A | DIN ISO 7619-1 |
| Viscosity (25°C) | 65 ± 20 | mPa.s | — |
| Compressive Strength | 47 ± 5 | MPa | EN ISO 604 |
| Density (20°C) | 1,10 ± 0,02 | g/cm3 | — |
| Flexural elongation at break | 12 ± 0.3 | % | EN ISO 178 |
| Pot Life (200g/20°C) | 2,5 - 3,5 | minutes | — |
| Flexural modulus | 1000 ± 100 | MPa | EN ISO 178 |
| Curing time at RT | 0,5 - 1,5 | Hrs | — |
| Flexural strength | 60 ± 5 | MPa | EN ISO 178 |
| Heat resistance (HDT) | 84 ± 3 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 26 ± 2.5 | kJ/m2 | EN ISO 179 |