Ebalta Kunststoff Gmbh SG 700PUR 5
- Chemical Family
- Polyurethanes (PU)
Ebalta SG 700 / PUR 5 is a two-component-Polyurethane casting resin, which cures very fast at room temperature. The very good workability and the excellent mechanical properties makes SG 700 a material with versatile application possibilities. ebalta SG 700 A is even more abrasion-resistant, but not so well workable by machine. Displacements, even made of wood, can be filled in. Material should be carefully stirred up/ shaked before use.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Other Industrial Applications
- Tooling & Moldmaking
Product Families
Plastics — Thermoset Resins
- Polyurethanes
Other characteristics
- Density
- 1650.0 - 1750.0 kg/m³
- End Uses
Foundry Dressings, Industrial Castings, Modeling Material
- Polymer Name
- Polyurethane (unspecified)
- Processing Methods
- Casting
- Markets
- Industrial
- Storing
Storage at room temperature 18-25 °C.; Opened containers should be closed immediately after use and should be used up as soon as possible.
- Packages
- 8,000 kg / 50,000 kg
- 1,000 kg / 6,000 kg
- Properties
well castable fine structure dimensionally accurate fast curing multi purpose useable
- Technology
- Plastics
- Material Features
- Excellent Dimensional Accuracy
- Fast Curing
- Plastics and Elastomers End Uses
- Foundry Dressings
- Industrial Castings
- Modeling Material
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Casting
Technical data
Table 1 of 1
19 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 83 ± 3 | Shore D | DIN ISO 7619-1 |
| Compressive Strength | 60 ± 5 | MPa | EN ISO 604 |
| Viscosity (25°C) | 3050 ± 250 | mPa.s | — |
| Flexural elongation at break | 1.1 ± 0.1 | % | EN ISO 178 |
| Density (20°C) | 1,70 ± 0,05 | g/cm3 | — |
| Flexural modulus | 4500 ± 400 | MPa | EN ISO 178 |
| Pot Life (200g/20°C) | 5-6 | minutes | — |
| Flexural strength | 40 ± 4 | MPa | EN ISO 178 |
| Curing time at RT | 1-2 | Hrs | — |
| Heat resistance (HDT) | 78 ± 3 | °C | DIN EN ISO 75 B |
| Flexural Strength | 40 ± 4 | MPa | EN ISO 178 |
| Impact resistance (Charpy) | 4 ± 0.5 | kJ/m2 | EN ISO 179 |