Ebalta Kunststoff Gmbh Silastic RTV 4260 V
- Chemical Family
- Silicones
SILASTIC RTV-4260-V Kit is a two-component material consisting of a SILASTIC™ RTV4260-V Base, which when mixed with the SILASTIC™ RTV-4260-V Curing Agent cures at room temperature by an addition reaction. A range of materials can be cast into the cured silicone mold: plaster, polyurethane, and concrete are materials typically used.
Product families
Elastomers — Specialty Elastomers
- Silicone Elastomers
Other characteristics
- End Uses
- Furniture, Modeling Material
- Features
Dimensional Stability, Good Mold Release, High Elasticity, High Strength, Low Shrinkage, Medium Hardness, Medium Viscosity, Tear Resistance, Thixotropic
- Polymer Name
- Silicone Elastomer
- Markets
- Consumer Goods
- Industrial
- Limitations
This product is neither tested nor represented as suitable for medical or pharmaceutical uses.; Not intended for human injection. Not intended for food use
- Technology
- Elastomers
Technical data
Table 1 of 1
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Base Viscosity | 56000 | mPa.s |
| Curing Agent Viscosity | 300 | mPa.s |
| Base and Curing Agent Mixture (100:10 by weight,Viscosity) | 19000 | mPa.s |
| Base and Curing Agent Mixture (100:10 by weight,Working time at 23°C) | 60–90 | minutes |
| Base and Curing Agent Mixture (100:10 by weight,Specific gravity) | 1.35 | g/cc |
| Hardness Cured for 24 hours at 23°C | 38 | Shore A |
| Tear strength, Die B Cured For 24 Hours At 23°C | 182 | ppi |
| Tear strength, Die B Cured For 24 Hours At 23°C | 32 | kN/m |
| Elongation at Break Cured for 24 hours at 23°C | 500 | % |
| Tensile strength Cured for 24 hours at 23°C | 913 | psi |
| Tensile strength Cured for 24 hours at 23°C | 6.3 | MPa |
| Linear shrinkage Cured for 24 hours at 23°C | max. 0.1 | % |