Ebalta Kunststoff Gmbh AH 140TC 60
- Chemical Family
- Epoxy & Epoxy Derivatives
Ebalta AH 140 / TC 60 is a temperature resistant laminating resin.
Product families
Applications
- Exterior & Body
- Interior
- Other Automotive Applications
- Aerospace & Aviation
- Marine
Product Families
- Epoxies
Other characteristics
- End Uses
Aerospace Applications, Aircraft Applications, Aircraft Interiors, Automotive Applications, Automotive Exterior Parts, Automotive Interior Parts, Laminates, Marine Applications
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 110.0 - 130.0 MPa
- Processing Methods
- Laminating
- Basis
- Temperature resistant laminating resin
- Markets
- Automotive & Transportation
- Storing
At appropriate storage 18-25°C.; Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours.; Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible.
- Properties
low viscosity good curing at room temperature high strength high heat resistance excellent wet-out characteristics
- Cure
- Chemical Cure
- Technology
- Plastics
- Material Features
- High Strength
- Low Viscosity
- Very Good Heat Resistance
- Processing Instruction
The temperature of material and processing should be between 18 and 25° C.; The mixing of resin and hardener should be made intensively and if possible without any bubbles at room temperature.; Additonal details for post curing:; 24 h at RT; 4 h at 60°C; 5 h at 80°C
- Plastics and Elastomers End Uses
- Aerospace Applications
- Aircraft Applications
- Aircraft Interiors
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Laminates
- Marine Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Laminating
Technical data
Table 1 of 1
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 86 ± 3 | Shore D | DIN ISO 7619-1 |
| Viscosity (25°C) | 600 ± 75 | mPa.s | — |
| Compressive Strength | 85 ± 8 | MPa | EN ISO 604 |
| Density (20°C) | 1,10 ± 0,02 | g/cm3 | — |
| Flexural elongation at break | 7.5 ± 0.4 | % | EN ISO 178 |
| Pot Life (200g/20°C) | 55 - 65 | minutes | — |
| Flexural modulus | 2900 ± 300 | MPa | EN ISO 178 |
| Curing time at RT | 22 - 26 | Hrs | — |
| Flexural strength | 120 ± 10 | MPa | EN ISO 178 |
| Post Curing | 4 - 6 (5 - 6) | Time in h (Temperature in °C) | — |
| Glass transition temperature TG | 93 | °C | — |
| Heat resistance (HDT) | 97 ± 3 | °C | DIN EN ISO 75 B |